Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 24 g/10 min |
| Shrinkage rate | | 内部方法 | 0.50 - 0.70 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-2 |
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 96.0 Mpa |
| elongation | | ASTM D638 | 70 % |
| Flexural modulus | | ASTM D790 | 3170 Mpa |
| bending strength | | ASTM D790 | 144 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Suspended wall beam without notch impact strength | | ASTM D4812 | 2100 J/m |
| Reverse notch impact | | ASTM D256 | 2100 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 4 |
| High arc combustion index (HAI) | | UL 746 | PLC 4 |
| Hot wire ignition (HWI) | | UL 746 | PLC 0 |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 135 °C |
| drying time | | | 4.0 to 6.0 hr |
| Suggested maximum moisture content | | | 0.020 % |
| Suggested injection volume | | | 40 to 60 % |
| Temperature at the rear of the barrel | | | 340 to 360 °C |
| Temperature in the middle of the barrel | | | 345 to 365 °C |
| Temperature at the front of the material cylinder | | | 350 to 370 °C |
| Spray nozzle temperature | | | 350 to 370 °C |
| Processing (melt) temperature | | | 350 to 370 °C |
| Temperature | | | 135 to 165 °C |
| Back pressure | | | 0.300 to 0.700 Mpa |
| screw speed | | | 40 to 70 rpm |
| Exhaust hole depth | | | 0.025 to 0.076 mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 190 °C |
| RTI Elec | | UL 746 | 115 °C |
| RTI Imp | | UL 746 | 115 °C |
| RTI | | UL 746 | 115 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.