PEI ATX200 BK1343 SABIC INNOVATIVE US
ULTEM™
Automotive sector、Electrical field、Electronic field
Glass fiber reinforced、Flame retardant、enhance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/ATX200 BK1343 |
|---|---|---|---|
| RTI | UL 746 | 115 °C | |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 190 °C |
| RTI Imp | UL 746 | 115 °C | |
| RTI Elec | UL 746 | 115 °C |
| Injection | Test Condition | Test Method | SABIC INNOVATIVE US/ATX200 BK1343 |
|---|---|---|---|
| Middle Temperature | 345 到 365 °C | ||
| Drying Time | 4.0 到 6.0 hr | ||
| Suggested Shot Size | 40 到 60 % | ||
| Drying Temperature | 135 °C | ||
| Mold Temperature | 135 到 165 °C | ||
| Vent Depth | 0.025 到 0.076 mm | ||
| Suggested Max Moisture | 0.020 % | ||
| Processing (Melt) Temp | 350 到 370 °C | ||
| Rear Temperature | 340 到 360 °C | ||
| Nozzle Temperature | 350 到 370 °C | ||
| Front Temperature | 350 到 370 °C | ||
| Back Pressure | 0.300 到 0.700 Mpa | ||
| Screw Speed | 40 到 70 rpm |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/ATX200 BK1343 |
|---|---|---|---|
| Melt Mass-Flow Rate | 337°C/6.6 kg | ASTM D1238 | 24 g/10 min |
| Modeling Shrinkage - Flow | 3.20 mm | 内部方法 | 0.50 到 0.70 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/ATX200 BK1343 |
|---|---|---|---|
| Tensile Strength | 屈服 | ASTM D638 | 96.0 Mpa |
| Flexural Modulus | 100 mm 跨距 | ASTM D790 | 3170 Mpa |
| Tensile Elongation | 断裂 | ASTM D638 | 70 % |
| Flexural Strength | 屈服, 100 mm 跨距 | ASTM D790 | 144 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/ATX200 BK1343 |
|---|---|---|---|
| Unnotched Izod Impact Strength | 23°C | ASTM D4812 | 2100 J/m |
| Reverse Notch Izod Impact | 3.20 mm | ASTM D256 | 2100 J/m |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/ATX200 BK1343 |
|---|---|---|---|
| UL flame retardant rating | 0.75 mm | UL 94 | V-2 |
| 1.5 mm | UL 94 | V-0 |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/ATX200 BK1343 |
|---|---|---|---|
| Hot-wire Ignition | UL 746 | PLC 0 | |
| Comparative Tracking Index | UL 746 | PLC 4 | |
| High Amp Arc Ignition | UL 746 | PLC 4 |