PA610 LNP™ THERMOCOMP™ QCL-4036 BK
139
- Properties:Thermal stabilityConductiveGlass fiber reinforced
- Usages:Electronic and Electrical ApplicationsFitness equipment
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.060-0.080 % | |
| ASTM D955 | 0.40-0.60 % | ||
| Water absorption rate | ASTM D570 | 0.19 % | |
| ISO 62 | 0.30 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Wear factor | ASTM D3702Modified | 26.0 10^-10in^5-min/ft-lb-hr | |
| Tensile modulus | ASTM D638 | 16600 Mpa | |
| ISO 527-2/1 | 15600 Mpa | ||
| tensile strength | ASTM D638 | 201 Mpa | |
| ISO 527-2/5 | 197 Mpa | ||
| elongation | ASTM D638 | 2.7 % | |
| Tensile strain | ISO 527-2/5 | 2.7 % | |
| Flexural modulus | ASTM D790 | 12400 Mpa | |
| ISO 178 | 12500 Mpa | ||
| bending strength | ISO 178 | 280 Mpa | |
| ASTM D790 | 289 Mpa | ||
| ASTM D790 | 288 Mpa | ||
| coefficient of friction | ASTM D3702Modified | 0.39 | |
| ASTM D3702Modified | 0.33 | ||
| Wear factor | ASTM D3702Modified | 0.300 10^-10in^5-min/ft-lb-hr |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO 180/1A | 10 kJ/m² | |
| Suspended wall beam without notch impact strength | ISO 180/1U | 53 kJ/m² | |
| Dart impact | ASTM D3763 | 10.0 J | |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 3.58 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/Bf | 221 °C | |
| ASTM D648 | 212 °C | ||
| ISO 75-2/Af | 206 °C | ||
| Linear coefficient of thermal expansion | ASTM D696 | 2.1E-05 cm/cm/°C | |
| ASTM D696 | 5.8E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.