Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA610 QCL-4036 BK SABIC INNOVATIVE US
LNP™ THERMOCOMP™
Electronic and Electrical、Fitness equipment
Thermal stability、Conductive、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/QCL-4036 BK |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 53 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 10.0 J |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 3.58 J | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 10 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/QCL-4036 BK |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 15600 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 197 Mpa |
| Wear factor | Washer | ASTM D3702Modified | 26.0 10^-10in^5-min/ft-lb-hr |
| tensile strength | 断裂 | ASTM D638 | 201 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 12400 Mpa |
| Tensile modulus | ASTM D638 | 16600 Mpa | |
| elongation | 断裂 | ASTM D638 | 2.7 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 289 Mpa |
| ISO 178 | 280 Mpa | ||
| coefficient of friction | Static | ASTM D3702Modified | 0.33 |
| Flexural modulus | ISO 178 | 12500 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 2.7 % |
| Wear factor | Ring | ASTM D3702Modified | 0.300 10^-10in^5-min/ft-lb-hr |
| coefficient of friction | Dynamic | ASTM D3702Modified | 0.39 |
| bending strength | 断裂,50.0mm跨距 | ASTM D790 | 288 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/QCL-4036 BK |
|---|---|---|---|
| Shrinkage rate | MD：24小时 | ASTM D955 | 0.060-0.080 % |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.19 % |
| 平衡,23°C,50%RH | ISO 62 | 0.30 % | |
| Shrinkage rate | TD：24hr | ASTM D955 | 0.40-0.60 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/QCL-4036 BK |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 221 °C |
| Linear coefficient of thermal expansion | MD：-30到30°C | ASTM D696 | 2.1E-05 cm/cm/°C |
| TD：-30to30°C | ASTM D696 | 5.8E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 206 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 212 °C |