Biodeg Polymers F 6510
0
- Usages:Thin filmcast film
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.30 g/cm³ | |
| Apparent density | ISO 60 | 0.80 g/cm³ | |
| melt mass-flow rate | ISO 1133 | 2.5to4.5 g/10min | |
| Melt volume flow rate | ISO 1133 | 2.50to4.50 cm³/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | ISO 178 | 64.0 MPa | |
| Tensile strain change rate | ISO 527 | 4.0 % | |
| Tensile modulus | ISO 527-2 | 2600 MPa | |
| tensile strength | Yield | ISO 527-2 | 47.0 MPa |
| Break | ISO 527-2 | 23.0 MPa | |
| Tensile strain | Break | ISO 527-2 | 19 % |
| Flexural modulus | ISO 178 | 2650 MPa | |
| Fracture bending strain | ISO 178 | NoBreak % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 7.0 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179/1eU | 无断裂 |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water Vapor Transmission Rate | ISO 15106-3 | 130 g/m²/24hr | |
| OTr | ISO 15105-2 | 1.1 cm³/m²/bar/24hr | |
| Nitrogen permeation rate | DIN 53380-2 | 150 cm³/m²/bar/24hr |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ISO 306/A | 60.0 °C | |
| melting temperature | ISO 3146 | 150to170 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.