Biodeg Polymers F 6510 FKuR Kunststoff GmbH
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | FKuR Kunststoff GmbH/F 6510 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 7.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| film | Test Condition | Test Method | FKuR Kunststoff GmbH/F 6510 |
|---|---|---|---|
| Water Vapor Transmission Rate | 20µm | ISO 15106-3 | 130 g/m²/24hr |
| Nitrogen permeation rate | 20.0µm | DIN 53380-2 | 150 cm³/m²/bar/24hr |
| OTr | 20.0µm | ISO 15105-2 | 1.1 cm³/m²/bar/24hr |
| Mechanical properties | Test Condition | Test Method | FKuR Kunststoff GmbH/F 6510 |
|---|---|---|---|
| bending strength | 3.5%应变 | ISO 178 | 64.0 MPa |
| Tensile modulus | ISO 527-2 | 2600 MPa | |
| tensile strength | 断裂 | ISO 527-2 | 23.0 MPa |
| Tensile strain | 断裂 | ISO 527-2 | 19 % |
| tensile strength | 屈服 | ISO 527-2 | 47.0 MPa |
| Tensile strain change rate | ISO 527 | 4.0 % | |
| Flexural modulus | ISO 178 | 2650 MPa | |
| Fracture bending strain | ISO 178 | NoBreak % |
| physical property | Test Condition | Test Method | FKuR Kunststoff GmbH/F 6510 |
|---|---|---|---|
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 2.50to4.50 cm³/10min |
| Apparent density | ISO 60 | 0.80 g/cm³ | |
| density | ISO 1183 | 1.30 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 2.5to4.5 g/10min |
| Thermal performance | Test Condition | Test Method | FKuR Kunststoff GmbH/F 6510 |
|---|---|---|---|
| vicat | ISO 306/A | 60.0 °C | |
| melting temperature | ISO 3146 | 150to170 °C |