Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ISO 1110 | 2.6to3.4 % |
| density | | ISO 1183 | 1.13 g/cm³ |
| spiral flow length | | 内部方法 | 107 cm |
| Shrinkage rate | | ISO 294-4 | 1.0 % |
| Shrinkage rate | | ISO 294-4 | 1.1 % |
| Water absorption rate | | ISO 62 | 9.0to10 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | FMVSS302 | <100 mm/min |
| UL flame retardant rating | | UL 94 | V-2 |
| Burning wire flammability index | | IEC 60695-2-12 | 750 °C |
| GWIT | | IEC 60695-2-13 | 675 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1 | 3600 MPa |
| tensile strength | Yield | ISO 527-2/50 | 85.0 MPa |
| Tensile strain | Break | ISO 527-2/50 | 20 % |
| Flexural modulus | | ISO 178 | 3100 MPa |
| bending strength | | ISO 178 | 120 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 2.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 5.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | NoBreak |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | NoBreak |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1E+12 ohms |
| Volume resistivity | | IEC 60093 | 1E+13 ohms·cm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| TemperatureIndex | | IEC 216 | 100to140 °C |
| Heat distortion temperature | | ISO 75-2/B | 180 °C |
| Heat distortion temperature | | ISO 75-2/A | 60.0 °C |
| melting temperature | | DIN EN11357-1 | 220 °C |
| TemperatureIndex | | IEC 216 | 90to120 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.