PA6 B3 natural (2500) AKRO-PLASTIC GmbH
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | AKRO-PLASTIC GmbH/ B3 natural (2500) |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.0 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 2.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Electrical performance | Test Condition | Test Method | AKRO-PLASTIC GmbH/ B3 natural (2500) |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+13 ohms·cm | |
| Surface Resistivity | IEC 60093 | 1E+12 ohms | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 0 |
| Mechanical properties | Test Condition | Test Method | AKRO-PLASTIC GmbH/ B3 natural (2500) |
|---|---|---|---|
| Flexural modulus | ISO 178 | 3100 MPa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 20 % |
| Tensile modulus | ISO 527-2/1 | 3600 MPa | |
| tensile strength | 屈服 | ISO 527-2/50 | 85.0 MPa |
| bending strength | ISO 178 | 120 MPa |
| flammability | Test Condition | Test Method | AKRO-PLASTIC GmbH/ B3 natural (2500) |
|---|---|---|---|
| burning rate | 1.00mm | FMVSS302 | <100 mm/min |
| Burning wire flammability index | 1.6mm | IEC 60695-2-12 | 750 °C |
| GWIT | 1.6mm | IEC 60695-2-13 | 675 °C |
| UL flame retardant rating | 1.6mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | AKRO-PLASTIC GmbH/ B3 natural (2500) |
|---|---|---|---|
| spiral flow length | 内部方法 | 107 cm | |
| density | 23°C | ISO 1183 | 1.13 g/cm³ |
| Shrinkage rate | TD | ISO 294-4 | 1.0 % |
| MD | ISO 294-4 | 1.1 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 9.0to10 % |
| 70°C | ISO 1110 | 2.6to3.4 % |
| Thermal performance | Test Condition | Test Method | AKRO-PLASTIC GmbH/ B3 natural (2500) |
|---|---|---|---|
| TemperatureIndex | 50%LossofTensileStrength,20000hr | IEC 216 | 90to120 °C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 180 °C |
| melting temperature | DIN EN11357-1 | 220 °C | |
| TemperatureIndex | 50%LossofTensileStrength,5000hr | IEC 216 | 100to140 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 60.0 °C |