Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.21 g/cm³ |
| Melt volume flow rate | | ISO1133 | 17.0 cm³/10min |
| Shrinkage rate | | ISO294-4 | 0.30到0.60 % |
| Shrinkage rate | | ISO294-4 | 0.50 % |
| Shrinkage rate | | ISO294-4 | 0.60 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO2039-1 | 115 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| Burning wire flammability index | | IEC60695-2-12 | 550 °C |
| FirePerformance | | FMVSS | passed |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| TristimulusValue | | DIN5033 | 92 % |
| TristimulusValue | | ISO13468 | 0.40 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 13 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 100 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 2700 MPa |
| Tensile stress | Yield | ISO527-2 | 50.0 MPa |
| Tensile stress | Break | ISO527-2 | 39.0 MPa |
| Tensile strain | Yield | ISO527-2 | 3.0 % |
| Tensile strain | Break | ISO527-2 | 13 % |
| Flexural modulus | | ISO178 | 2700 MPa |
| Bending stress | | ISO178 | 75.0 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 100 °C |
| vicat | | ISO306/B50 | 109 °C |
| BallPressure Test | | IEC60695-10-2 | 通过 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare