ABS AWL 109/15 WT1217-11LB ALBIS PLASTIC GmbH
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodALBIS PLASTIC GmbH/ AWL 109/15 WT1217-11LB
Impact strength of simply supported beam without notchISO 179/1eU100 kJ/m²
Charpy Notched Impact StrengthISO 179/1eA13 kJ/m²
Supplementary InformationTest ConditionTest MethodALBIS PLASTIC GmbH/ AWL 109/15 WT1217-11LB
TristimulusValueY10ofTransmittance:500.0µmISO 134680.40 %
Y10ofReflectionDIN 503392 %
hardnessTest ConditionTest MethodALBIS PLASTIC GmbH/ AWL 109/15 WT1217-11LB
ball-indentation hardnessH358/30ISO 2039-1115 MPa
Mechanical propertiesTest ConditionTest MethodALBIS PLASTIC GmbH/ AWL 109/15 WT1217-11LB
Tensile modulusISO 527-22700 MPa
tensile strength 断裂ISO 527-239.0 MPa
Tensile strain断裂ISO 527-213 %
屈服ISO 527-23.0 %
tensile strength 屈服ISO 527-250.0 MPa
Flexural modulusISO 1782700 MPa
bending strengthISO 17875.0 MPa
flammabilityTest ConditionTest MethodALBIS PLASTIC GmbH/ AWL 109/15 WT1217-11LB
UL flame retardant rating3.0mmUL 94HB
2.00mmFMVSSpassed
1.5mmUL 94HB
Burning wire flammability index2.0mmIEC 60695-2-12550 °C
physical property Test ConditionTest MethodALBIS PLASTIC GmbH/ AWL 109/15 WT1217-11LB
Shrinkage rateMD:24小时ISO 294-40.60 %
Melt volume flow rate220°C/10.0kgISO 113317.0 cm³/10min
Shrinkage rate--ISO 294-40.30to0.60 %
densityISO 11831.21 g/cm³
Shrinkage rateTD:24小时ISO 294-40.50 %
Thermal performanceTest ConditionTest MethodALBIS PLASTIC GmbH/ AWL 109/15 WT1217-11LB
vicatISO 306/B50109 °C
Heat distortion temperature1.8MPa,未退火，HDTISO 75-2/A100 °C
ball-indentation hardness100°CIEC 60695-10-2通过