| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ISO 62 | 0.060 % |
| Shrinkage rate | | 内部方法 | 0.50-0.70 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-1 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527-2 | 46.0 Mpa |
| Nominal tensile fracture strain | | ISO 527-2 | 30 % |
| Flexural modulus | | ISO 178 | 2000 Mpa |
| bending strength | | ISO 178 | 78.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179 | 6.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC 60093 | 1E+16 ohms·cm |
| Surface Resistivity | | IEC 60093 | 1E+16 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| 1.8MPa, Not annealed | | ASTM D648 | 100 °C |
| 1.8MPa, Not annealed | | ISO 75-2/A | 96.0 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 7.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.