Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | % | 1.0 -- |
| Shrinkage rate | | % | 0.30 -- |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | | V-0 -- |
| Flammability level | | | V-0 -- |
| Burning wire flammability index | | °C | 960 -- |
| Burning wire flammability index | | °C | 960 -- |
| Hot filament ignition temperature | | °C | 700 -- |
| Hot filament ignition temperature | | °C | 775 -- |
| Limiting Oxygen Index | | % | 37 -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | MPa | 10700 11300 |
| Tensile stress | | MPa | 145 |
| Tensile strain | | % | 2.1 1.9 |
| Flexural modulus | | MPa | 9800 10800 |
| Bending stress | | MPa | 225 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | kJ/m² | 40 |
| Impact strength of simply supported beam without notch | | kJ/m² | 45 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| CTI | | V | 600 -- |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| RTI Elec | | °C | 140 -- |
| RTI Elec | | °C | 140 -- |
| RTI Elec | | °C | 140 -- |
| RTI Elec | | °C | 140 -- |
| Heat distortion temperature | | °C | 281 -- |
| Melting temperature 1 | | °C | 310 -- |
| | cm/cm/°C | 1.8E-05 -- |
| | cm/cm/°C | 1.8E-05 -- |
| | cm/cm/°C | 1.2E-05 -- |
| | cm/cm/°C | 6.2E-05 -- |
| | cm/cm/°C | 6E-05 -- |
| | cm/cm/°C | 9.5E-05 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.