PA66 FR52G30NH DUPONT JAPAN
Zytel®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT JAPAN/FR52G30NH |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | kJ/m² | 40 |
| 23°C | kJ/m² | 45 |
| Mechanical properties | Test Condition | Test Method | DUPONT JAPAN/FR52G30NH |
|---|---|---|---|
| Flexural modulus | MPa | 9800 10800 | |
| Bending stress | MPa | 225 | |
| Tensile modulus | MPa | 10700 11300 | |
| Tensile stress | 断裂 | MPa | 145 |
| Tensile strain | 断裂 | % | 2.1 1.9 |
| Electrical performance | Test Condition | Test Method | DUPONT JAPAN/FR52G30NH |
|---|---|---|---|
| CTI | V | 600 -- |
| flammability | Test Condition | Test Method | DUPONT JAPAN/FR52G30NH |
|---|---|---|---|
| Flammability level | 1.50mm | V-0 -- | |
| 0.400mm | V-0 -- | ||
| Hot filament ignition temperature | 3.00mm | °C | 775 -- |
| Limiting Oxygen Index | % | 37 -- | |
| Burning wire flammability index | 0.400mm | °C | 960 -- |
| Hot filament ignition temperature | 0.400mm | °C | 700 -- |
| Burning wire flammability index | 3.00mm | °C | 960 -- |
| physical property | Test Condition | Test Method | DUPONT JAPAN/FR52G30NH |
|---|---|---|---|
| Shrinkage rate | MD | % | 0.30 -- |
| TD | % | 1.0 -- |
| Thermal performance | Test Condition | Test Method | DUPONT JAPAN/FR52G30NH |
|---|---|---|---|
| MD:-40到23°C | cm/cm/°C | 1.8E-05 -- | |
| Heat distortion temperature | 1.8MPa,未退火 | °C | 281 -- |
| MD | cm/cm/°C | 1.8E-05 -- | |
| Melting temperature 1 | °C | 310 -- | |
| RTI Elec | 3.00mm | °C | 140 -- |
| MD:55到160°C | cm/cm/°C | 1.2E-05 -- | |
| RTI Elec | 0.750mm | °C | 140 -- |
| TD | cm/cm/°C | 6.2E-05 -- | |
| RTI Elec | 0.400mm | °C | 140 -- |
| 1.50mm | °C | 140 -- | |
| TD:-40到23°C | cm/cm/°C | 6E-05 -- | |
| TD:55到160°C | cm/cm/°C | 9.5E-05 -- |