Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.48 g/cm³ |
| density | | ISO 1183 | 1.48 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 15 g/10min |
| melt mass-flow rate | | ISO 1133 | 15 g/10min |
| Shrinkage rate | | ASTM D955 | 0.16 % |
| Shrinkage rate | | ISO 2577 | 0.16 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | Break | ASTM D638 | 3.0 % |
| Tensile strain | Break | ISO 527-2 | 3.0 % |
| Flexural modulus | | ASTM D790 | 7000 MPa |
| Flexural modulus | | ISO 178 | 7000 MPa |
| bending strength | | ASTM D790 | 190 MPa |
| Tensile modulus | | ASTM D638 | 9800 MPa |
| Tensile modulus | | ISO 527-2 | 9800 MPa |
| tensile strength | Yield | ASTM D638 | 130 MPa |
| tensile strength | Yield | ISO 527-2 | 130 MPa |
| bending strength | | ISO 178 | 190 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 85 J/m |
| Impact strength of cantilever beam gap | | ISO 180 | 10 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | IEC 60250 | 3.70 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 206 °C |
| Heat distortion temperature | | ISO 75-2/B | 205 °C |
| Heat distortion temperature | | ASTM D648 | 170 °C |
| Heat distortion temperature | | ISO 75-2/A | 170 °C |
| melting temperature | | ASTM D3418 | 220 °C |
| melting temperature | | ISO 11357-3 | 220 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.