Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.47 g/cm³ |
| Shrinkage rate | | 内部方法 | 0.15to0.25 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Limiting Oxygen Index | | ISO 4589-2 | 25 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | Break | ISO 527-2/5 | 2.0 % |
| Flexural modulus | | ISO 178 | 12000 MPa |
| bending strength | | ISO 178 | 290 MPa |
| Tensile modulus | | ISO 527-2/1 | 13500 MPa |
| tensile strength | Break | ISO 527-2/5 | 195 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 150 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 15 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 16 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 17 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 2 |
| Surface Resistivity | | IEC 60093 | >1.0E+16 ohms |
| Volume resistivity | | IEC 60093 | >1.0E+16 ohms·cm |
| dielectric strength | | IEC 60243-1 | 20 kV/mm |
| relative permittivity | | IEC 60250 | 3.60 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 1 |
| relative permittivity | | IEC 60250 | 3.60 |
| relative permittivity | | IEC 60250 | 3.40 |
| Dissipation Factor | | IEC 60250 | 6.1E-03 |
| Dissipation Factor | | IEC 60250 | 6.1E-03 |
| Dissipation Factor | | IEC 60250 | 0.016 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/Be | 224 °C |
| Heat distortion temperature | | ISO 75-2/Ae | 212 °C |
| vicat | | ISO 306/B120 | 220 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1.7E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 8.2E-05 cm/cm/°C |
| thermal conductivity | | ISO 8302 | 0.33 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.