| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.56 g/cm³ |
| Shrinkage rate | | ASTM D955 | 0.20to0.30 % |
| Water absorption rate | | ASTM D570 | 0.80 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Hot filament ignition temperature | | IEC 60695-2-13 | 600 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ISO 178 | 6700 MPa |
| bending strength | | ISO 178 | 250 MPa |
| tensile strength | Yield | ISO 527-2 | 160 MPa |
| Tensile strain | Break | ISO 527-2 | 1.7 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 140 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTM D149 | 21 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 1 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 2 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO 306/B120 | 215 °C |
| Heat distortion temperature | | ISO 75-2/A | 200 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.