ABS M220 ELIX POLYMERS SPANISH

26

Technical Data Sheet

physical property Test ConditionTest MethodTest Result
melt mass-flow rateASTM D123811 g/10 min
Melt volume flow rateISO 113332.0 cm3/10min
Shrinkage rateISO 294-40.60 %
Shrinkage rateISO 294-40.60 %
hardnessTest ConditionTest MethodTest Result
ball-indentation hardnessISO 2039-1103 Mpa
Mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulusASTM D6382300 Mpa
Tensile modulusISO 527-2/12300 Mpa
tensile strength ASTM D63837.9 Mpa
tensile strength ISO 527-2/5041.0 Mpa
Flexural modulusASTM D7902200 Mpa
Flexural modulusISO 1782200 Mpa
bending strengthISO 17865.0 Mpa
Impact resistanceTest ConditionTest MethodTest Result
Impact strength of simply supported beam without notchISO 179/1eU80 kJ/m²
Impact strength of simply supported beam without notchISO 179/1eU100 kJ/m²
Electrical performanceTest ConditionTest MethodTest Result
Surface ResistivityIEC 600931.0E+16 ohms
Volume resistivityIEC 600931.0E+18 ohms·cm
dielectric strengthIEC 60243-135 KV/mm
relative permittivityIEC 602502.90
relative permittivityIEC 602502.90
Dissipation FactorIEC 602507.3E-3
Dissipation FactorIEC 602509.0E-3
injectionTest ConditionTest MethodTest Result
Processing (melt) temperature240 °C
Temperature80 °C
injection speedISO 29414 m/min
Thermal performanceTest ConditionTest MethodTest Result
Heat distortion temperatureISO 75-2/B97.0 °C
Heat distortion temperatureISO 75-2/A92.0 °C
vicatASTM D1525795.0 °C
vicatISO 306/B12097.0 °C
Linear coefficient of thermal expansionISO 11359-21.0E-4 cm/cm/°C
Linear coefficient of thermal expansionISO 11359-21.0E-4 cm/cm/°C
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.