ABS B3 2 RM-D natural (3293)

Usages:
Application in the automotive field
external parts of automobiles
internal parts of automobiles
Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density		ISO 1183	1.07 g/cm³
spiral flow length		内部方法	55.0 cm
Shrinkage rate		ISO 294-4	1.1 %
Shrinkage rate	Shrinkage rate		ISO 294-4	0.90 %
Water absorption rate		ISO 1110	1.6 %

flammability	Test Condition	Test Method	Test Result
burning rate		FMVSS302	<100 mm/min
UL flame retardant rating		UL 94	HB

Mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	70.0 MPa
Flexural modulus		ISO 178	2100 MPa
Tensile modulus		ISO 527-2/1	2000 MPa
tensile strength	Yield	ISO 527-2/50	47.0 MPa
Tensile strain	Break	ISO 527-2/50	>50 %

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO 179/1eA	15 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO 179/1eA	70 kJ/m²
Impact strength of simply supported beam without notch		ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch		ISO 179/1eU	NoBreak

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ISO 75-2/B	100 °C
Heat distortion temperature	Heat distortion temperature		ISO 75-2/A	67.0 °C
vicat		ISO 306/B50	112 °C
melting temperature		DIN EN11357-1	225 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.