ABS B3 2 RM-D natural (3293) AKRO-PLASTIC GmbH
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | AKRO-PLASTIC GmbH/ B3 2 RM-D natural (3293) |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 70 kJ/m² |
Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 15 kJ/m² |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
Mechanical properties | Test Condition | Test Method | AKRO-PLASTIC GmbH/ B3 2 RM-D natural (3293) |
---|---|---|---|
Flexural modulus | ISO 178 | 2100 MPa | |
Tensile strain | 断裂 | ISO 527-2/50 | >50 % |
Tensile modulus | ISO 527-2/1 | 2000 MPa | |
bending strength | ISO 178 | 70.0 MPa | |
tensile strength | 屈服 | ISO 527-2/50 | 47.0 MPa |
flammability | Test Condition | Test Method | AKRO-PLASTIC GmbH/ B3 2 RM-D natural (3293) |
---|---|---|---|
burning rate | 1.00mm | FMVSS302 | <100 mm/min |
UL flame retardant rating | 0.8mm | UL 94 | HB |
physical property | Test Condition | Test Method | AKRO-PLASTIC GmbH/ B3 2 RM-D natural (3293) |
---|---|---|---|
spiral flow length | 内部方法 | 55.0 cm | |
density | 23°C | ISO 1183 | 1.07 g/cm³ |
Shrinkage rate | TD | ISO 294-4 | 1.1 % |
MD | ISO 294-4 | 0.90 % | |
Water absorption rate | 70°C | ISO 1110 | 1.6 % |
Thermal performance | Test Condition | Test Method | AKRO-PLASTIC GmbH/ B3 2 RM-D natural (3293) |
---|---|---|---|
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/B | 100 °C |
melting temperature | DIN EN11357-1 | 225 °C | |
vicat | ISO 306/B50 | 112 °C | |
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/A | 67.0 °C |