Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.06 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 2.5 g/10min |
| Shrinkage rate | | ASTM D955 | 0.30to0.60 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 82 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | ASTM D1003 | 93.0 % |
| Haze ratio | | ASTM D1003 | 0.50 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Suspended wall beam without notch impact strength | | ASTM D256 | 32 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 2890 MPa |
| tensile strength | Yield | ASTM D638 | 63.0 MPa |
| elongation | Break | ASTM D638 | 6.0 % |
| Flexural modulus | | ASTM D790 | 3310 MPa |
| bending strength | Yield | ASTM D790 | 110 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 93.0 °C |
| vicat | | ASTM D15252 | 104 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare