PBT IQNH4550 7A5D006 SABIC INNOVATIVE US

Form：Granules

Properties:

Glass fiber reinforcedHigh impact resistance

Typical Applications:

Automotive ApplicationsElectrical applications

Supplier(2)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive Applications \| Electrical applications
Properties:	Glass fiber reinforced \| High impact resistance

Certificates

No Data...

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			玻璃纤维增强25%.无溴阻燃
purpose			IT办公
impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C,TotalEnergy	ASTM D3763	6.50	J
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	33	kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	29	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	7.0	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/2U	33	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/2U	36	kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	7.0	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning wire flammability index	0.75mm	IEC 60695-2-12	960	°C
UL flame retardant rating	3.0mm	UL 94	5VA
UL flame retardant rating	UL flame retardant rating	0.75mm	UL 94	V-0
Hot filament ignition temperature	0.8mm	IEC 60695-2-13	775	°C
Hot filament ignition temperature	Hot filament ignition temperature	3.0mm15	IEC 60695-2-13	775	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
elongation	Yield	ASTM D638	2.0	%
tensile strength	Yield	ASTM D638	105	Mpa
Tensile modulus		ISO 527-2/1	10400	Mpa
Tensile modulus	Tensile modulus		ASTM D638	9900	Mpa
tensile strength	Yield	ISO 527-2/5	112	Mpa
	tensile strength	Break	ASTM D638	105	Mpa
	tensile strength	tensile strength	Break	ISO 527-2/5	112	Mpa
Tensile strain	Yield	ISO 527-2/5	2.0	%
elongation	Break	ASTM D638	2.0	%
Tensile strain	Break	ISO 527-2/5	2.0	%
Bending modulus	50.0mmSpan	ASTM D790	9100	Mpa
Bending modulus	Bending modulus		ISO 178	9400	Mpa
bending strength		ISO 178	170	Mpa
bending strength	bending strength	Yield,50.0mmSpan	ASTM D790	161	Mpa
Fracture bending strain		ISO 178	2.0	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	219	°C
	Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	216	°C
		Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	204	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	201	°C
Linear coefficient of thermal expansion	TD：23to80°C	ISO 11359-2	9.1E-05	cm/cm/°C
Vicat softening temperature	--	ASTM D152512	215	°C
RTI Elec		UL 746	130	°C
RTI Imp		UL 746	140	°C
RTI Str		UL 746	140	°C
Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	7.1E-05	cm/cm/°C
	Linear coefficient of thermal expansion	TD：-40to150°C	ASTME831	7.7E-05	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	7.6E-05	cm/cm/°C
Vicat softening temperature	--	ASTM D152513	202	°C
	Vicat softening temperature	--	ISO 306/A50	219	°C
		Vicat softening temperature	--	ISO 306/B50	206	°C
		Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	206	°C
Ball Pressure Test	125°C	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	2.7E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to150°C	ASTME831	2.2E-05	cm/cm/°C
		Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	3E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23to80°C	ISO 11359-2	2.2E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.060	%
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.23	%
Shrinkage rate	TD：3.20mm	Internal Method	0.50-1.1	%
	Shrinkage rate	TD：--2	Internal Method	0.60-1.2	%
		Shrinkage rate	MD：3.20mm	Internal Method	0.10-0.50	%
		Shrinkage rate	Shrinkage rate	MD：--2	Internal Method	0.10-0.50	%
Melt Volume Flow Rate (MVR)	250°C/5.0kg	ISO 1133	20.0	cm3/10min
melt mass-flow rate	250°C/5.0kg	ASTM D1238	27	g/10min
MeltViscosity	250°C,1500sec^-1	ISO 11443	210	Pa·s
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Hot wire ignition	HWI	UL 746	PLC 0
High voltage arc tracing rate	HVTR	UL 746	PLC 0
Arc resistance		ASTM D495	PLC6
Dielectric strength	3.20mm,in Oil	ASTM D149	21	KV/mm
Volume resistivity		IEC 60093	1.0E+15to1.0E+16	ohms·cm
Dielectric strength	3.20mm,inAir	ASTM D149	21	KV/mm
Volume resistivity		ASTM D257	1.0E+15to1.0E+16	ohms·cm
High arc combustion index	HAI	UL 746	PLC 0
Compared to the anti leakage trace index	CTI	UL 746	PLC 2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PBT IQNH4550 7A5D006 SABIC INNOVATIVE US

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index