Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT IQNH4550 7A5D006 SABIC INNOVATIVE US
VALOX™
Automotive Applications、Electrical applications
Glass fiber reinforced、High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/IQNH4550 7A5D006 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 29 kJ/m² |
| 23°C | ISO 180/1U | 33 kJ/m² | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 6.50 J |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 7.0 kJ/m² |
| 23°C | ISO 180/1A | 7.0 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/2U | 36 kJ/m² |
| -30°C | ISO 179/2U | 33 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/IQNH4550 7A5D006 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 10400 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 112 Mpa |
| elongation | 屈服 | ASTM D638 | 2.0 % |
| Tensile strain | 屈服 | ISO 527-2/5 | 2.0 % |
| Flexural modulus | 50.0mmSpan | ASTM D790 | 9100 Mpa |
| tensile strength | 屈服 | ISO 527-2/5 | 112 Mpa |
| Tensile modulus | ASTM D638 | 9900 Mpa | |
| elongation | 断裂 | ASTM D638 | 2.0 % |
| tensile strength | Break | ASTM D638 | 105 Mpa |
| bending strength | Yield,50.0mmSpan | ASTM D790 | 161 Mpa |
| ISO 178 | 170 Mpa | ||
| Flexural modulus | ISO 178 | 9400 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 2.0 % |
| tensile strength | 屈服 | ASTM D638 | 105 Mpa |
| Fracture bending strain | ISO 178 | 2.0 % |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/IQNH4550 7A5D006 |
|---|---|---|---|
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 0 |
| Volume resistivity | ASTM D257 | 1.0E+15to1.0E+16 ohms·cm | |
| IEC 60093 | 1.0E+15to1.0E+16 ohms·cm | ||
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| dielectric strength | 3.20mm,在油中 | ASTM D149 | 21 KV/mm |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 0 |
| arc resistance | ASTM D495 | PLC6 | |
| dielectric strength | 3.20mm,inAir | ASTM D149 | 21 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| IEC 60112 | V |
| other | Test Condition | Test Method | SABIC INNOVATIVE US/IQNH4550 7A5D006 |
|---|---|---|---|
| characteristic | 玻璃纤维增强25%.无溴阻燃 | ||
| purpose | IT办公 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/IQNH4550 7A5D006 |
|---|---|---|---|
| Hot filament ignition temperature | 3.0mm15 | IEC 60695-2-13 | 775 °C |
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| 3.0mm | UL 94 | 5VA | |
| Burning wire flammability index | 0.75mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 0.8mm | IEC 60695-2-13 | 775 °C |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/IQNH4550 7A5D006 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.10-0.50 % |
| TD：--2 | 内部方法 | 0.60-1.2 % | |
| Melt volume flow rate | 250°C/5.0kg | ISO 1133 | 20.0 cm3/10min |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.50-1.1 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.060 % |
| Shrinkage rate | MD：--2 | 内部方法 | 0.10-0.50 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.23 % |
| MeltViscosity | 250°C,1500sec^-1 | ISO 11443 | 210 Pa·s |
| melt mass-flow rate | 250°C/5.0kg | ASTM D1238 | 27 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/IQNH4550 7A5D006 |
|---|---|---|---|
| vicat | -- | ASTM D152513 | 202 °C |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 216 °C |
| Linear coefficient of thermal expansion | TD：-40to40°C | ASTME831 | 7.1E-05 cm/cm/°C |
| RTI Str | UL 746 | 140 °C | |
| Heat distortion temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 219 °C |
| vicat | -- | ISO 306/B120 | 206 °C |
| -- | ASTM D152512 | 215 °C | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ISO 11359-2 | 3E-05 cm/cm/°C |
| vicat | -- | ISO 306/A50 | 219 °C |
| -- | ISO 306/B50 | 206 °C | |
| Linear coefficient of thermal expansion | TD：-40to40°C | ISO 11359-2 | 7.6E-05 cm/cm/°C |
| MD：-40to40°C | ASTME831 | 2.7E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 201 °C |
| RTI Imp | UL 746 | 140 °C | |
| Linear coefficient of thermal expansion | MD：23到80°C | ISO 11359-2 | 2.2E-05 cm/cm/°C |
| MD：-40to150°C | ASTME831 | 2.2E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 204 °C |
| Linear coefficient of thermal expansion | TD：-40to150°C | ASTME831 | 7.7E-05 cm/cm/°C |
| TD：23到80°C | ISO 11359-2 | 9.1E-05 cm/cm/°C | |
| RTI Elec | UL 746 | 130 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |