PBT LONGLITE® PBT 3020-200X
0
- Properties:Fillerglass fiber reinforced material20%filler by weight
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.45 g/cm³ | |
| Shrinkage rate | ISO 294-4 | 1.1-1.3 % | |
| ISO 294-4 | 0.3-0.5 % | ||
| melt mass-flow rate | ISO 1133 | 14 cm³/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 6500 MPa | |
| bending strength | ISO 178 | 175 MPa | |
| Flexural modulus | ISO 178 | 5500 MPa | |
| Charpy Notched Impact Strength | ISO 179/1eA | 8 kJ/m² | |
| tensile strength | ISO 527-2 | 115 MPa | |
| elongation at break | ISO 527-2 | 3.5 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+15 Ω.cm | |
| Surface Resistivity | IEC 60093 | 1E+15 Ω.cm | |
| dielectric strength | IEC 60243-1 | 25 KV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/Bf | 210 °C | |
| ISO 75-2/Af | 200 °C | ||
| vicat | Melting Temperature | ISO 11357-3 | 225 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.