PBT LONGLITE® PBT 3020-200X Chang Chun Plastics Co., Ltd. (CCP Group)
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | Chang Chun Plastics Co., Ltd. (CCP Group)/LONGLITE® PBT 3020-200X |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 1E+15 Ω.cm | |
| dielectric strength | 2.00mm | IEC 60243-1 | 25 KV/mm |
| Volume resistivity | IEC 60093 | 1E+15 Ω.cm |
| Mechanical properties | Test Condition | Test Method | Chang Chun Plastics Co., Ltd. (CCP Group)/LONGLITE® PBT 3020-200X |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178 | 5500 MPa |
| Tensile modulus | 23°C | ISO 527-2 | 6500 MPa |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 8 kJ/m² |
| tensile strength | 23°C | ISO 527-2 | 115 MPa |
| elongation at break | 23°C | ISO 527-2 | 3.5 % |
| bending strength | 23°C | ISO 178 | 175 MPa |
| physical property | Test Condition | Test Method | Chang Chun Plastics Co., Ltd. (CCP Group)/LONGLITE® PBT 3020-200X |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.3-0.5 % |
| MD | ISO 294-4 | 1.1-1.3 % | |
| melt mass-flow rate | 250℃/2.16Kg | ISO 1133 | 14 cm³/10min |
| density | ISO 1183 | 1.45 g/cm³ |
| Thermal performance | Test Condition | Test Method | Chang Chun Plastics Co., Ltd. (CCP Group)/LONGLITE® PBT 3020-200X |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 200 °C |
| vicat | 熔融温度 | ISO 11357-3 | 225 °C |
| Heat distortion temperature | 0.45MPa未退火，HDT | ISO 75-2/Bf | 210 °C |