PA6 M IMP NATURAL
0
- Properties:Improved impact resistancemedium impact resistance
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.06 to 1.08 g/cm³ | |
| Shrinkage rate | ISO 294-4 | 1.6 % | |
| 1.3 | |||
| Water absorption rate | ISO 62 | 0.20 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | ISO 178 | 50.0 to 60.0 MPa | |
| Charpy Notched Impact Strength | ISO 179/1eA | 40 to 60 kJ/m² | |
| Impact strength of cantilever beam gap | ISO 180/1A | 40 to 60 kJ/m² | |
| Hardness (Shore) | ISO 868 | 70 | |
| Tensile modulus | ISO 527-2 | 1900 to 2100 MPa | |
| tensile strength | ISO 527-2 | 45.0 to 55.0 MPa | |
| Tensile strain | ISO 527-2 | 60 to 80 % | |
| Flexural modulus | ISO 178 | 1700 to 1800 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature (HDT) | ISO 75-2/A | 53.0 ℃ | |
| melting temperature | ISO 3146 | 210 to 220 ℃ | |
| UL flame retardant rating | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.