PA6 M IMP NATURAL 土耳其EPSAN
--
--
改良抗撞击性,中等抗撞击性
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | 土耳其EPSAN/M IMP NATURAL |
|---|---|---|---|
| Hardness (Shore) | 支撐 D | ISO 868 | 70 |
| bending strength | 23℃ | ISO 178 | 50.0 to 60.0 MPa |
| tensile strength | 断裂, 23℃ | ISO 527-2 | 45.0 to 55.0 MPa |
| Flexural modulus | 23℃ | ISO 178 | 1700 to 1800 MPa |
| Tensile modulus | 23℃ | ISO 527-2 | 1900 to 2100 MPa |
| Impact strength of cantilever beam gap | 23℃ | ISO 180/1A | 40 to 60 kJ/m² |
| Tensile strain | 断裂, 23℃ | ISO 527-2 | 60 to 80 % |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 40 to 60 kJ/m² |
| physical property | Test Condition | Test Method | 土耳其EPSAN/M IMP NATURAL |
|---|---|---|---|
| Shrinkage rate | TD: 3.00 mm | ISO 294-4 | 1.6 % |
| Water absorption rate | 饱和, 23℃ | ISO 62 | 0.20 % |
| density | ISO 1183 | 1.06 to 1.08 g/cm³ | |
| Shrinkage rate | MD: 3.00 mm | 1.3 |
| Thermal performance | Test Condition | Test Method | 土耳其EPSAN/M IMP NATURAL |
|---|---|---|---|
| melting temperature | ISO 3146 | 210 to 220 ℃ | |
| Hot deformation temperature (HDT) | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 53.0 ℃ |
| UL flame retardant rating | 1.60 mm | UL 94 | HB |