PC+AS

PC+AS LNP™ LUBRICOMP™ Lexan_WR6300 compound SABIC

Usages:
Business equipment
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C,TotalEnergy	ASTM D3763	60.2 J
Impact strength of cantilever beam gap	23°C	ASTM D4812	2500 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D256	680 J/m
Dart impact	23°C,TotalEnergy	ASTM D3763	60.2 J
Suspended wall beam without notch impact strength	23°C	ASTM D4812	2500 J/m
Impact strength of cantilever beam gap	-30°C	ASTM D256	170 J/m
	Impact strength of cantilever beam gap	23°C	ASTM D256	680 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ASTM D256	170 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	1.50mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus	50.0mmSpan	ASTM D790	2490 MPa
tensile strength	Break	ASTM D638	61.4 MPa
tensile strength	tensile strength	Yield	ASTM D638	60.7 MPa
elongation	Break	ASTM D638	160 %
tensile strength	Break	ASTM D638	61.4 MPa
tensile strength	tensile strength	Yield	ASTM D638	60.7 MPa
bending strength	Yield,50.0mmSpan	ASTM D790	96.5 MPa
Bending modulus	50.0mmSpan	ASTM D790	2490 MPa
elongation	Break	ASTM D638	160 %
bending strength	Yield,50.0mmSpan	ASTM D790	96.5 MPa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	134 °C
	Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	134 °C
		Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	117 °C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	121 °C
Vicat softening temperature		ASTM D15254	137 °C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	1.1E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	1.2E-04 cm/cm/°C
RTI Elec		UL 746	80.0 °C
RTI Imp		UL 746	80.0 °C
RTI Str		UL 746	80.0 °C
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	117 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	121 °C
Vicat softening temperature		ASTM D15255	137 °C
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	1.1E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	1.2E-04 cm/cm/°C
RTI Elec		UL 746	80.0 °C
RTI Imp		UL 746	80.0 °C
RTI		UL 746	80.0 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD：3.20mm	Internal Method	0.50to0.70 %
Melt Volume Flow Rate (MVR)	300°C/2.16kg	ISO 1133	38.0 cm³/10min
density		ASTM D792	1.17 g/cm³
Shrinkage rate	MD：3.20mm	Internal Method	0.50to0.70 %
Melt Volume Flow Rate (MVR)	300°C/2.16kg	ISO 1133	38.0 cm³/10min
density		ASTM D792	1.17 g/cm³

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.