PC+AS LNP™ LUBRICOMP™ Lexan_WR6300 compound SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC/LNP™ LUBRICOMP™ Lexan_WR6300 compound
Impact strength of cantilever beam gap-30°CASTM D256170 J/m
Dart impact23°C,TotalEnergyASTM D376360.2 J
Impact strength of cantilever beam gap23°CASTM D256680 J/m
Suspended wall beam without notch impact strength23°CASTM D48122500 J/m
Impact strength of cantilever beam gap23°CASTM D48122500 J/m
Mechanical propertiesTest ConditionTest MethodSABIC/LNP™ LUBRICOMP™ Lexan_WR6300 compound
elongation断裂ASTM D638160 %
bending strength屈服,50.0mm跨距ASTM D79096.5 MPa
tensile strength 断裂ASTM D63861.4 MPa
Flexural modulus50.0mm跨距ASTM D7902490 MPa
tensile strength 屈服ASTM D63860.7 MPa
flammabilityTest ConditionTest MethodSABIC/LNP™ LUBRICOMP™ Lexan_WR6300 compound
UL flame retardant rating1.50mmUL 94HB
1.5mmUL 94HB
physical property Test ConditionTest MethodSABIC/LNP™ LUBRICOMP™ Lexan_WR6300 compound
Shrinkage rateMD：3.20mm内部方法0.50to0.70 %
densityASTM D7921.17 g/cm³
Melt volume flow rate300°C/2.16kgISO 113338.0 cm³/10min
Thermal performanceTest ConditionTest MethodSABIC/LNP™ LUBRICOMP™ Lexan_WR6300 compound
Heat distortion temperature1.8MPa,未退火,6.40mm，HDTASTM D648121 °C
vicatASTM D15254137 °C
Linear coefficient of thermal expansionMD：-40到40°CASTME8311.1E-04 cm/cm/°C
Heat distortion temperature0.45MPa,未退火,6.40mm，HDTASTM D648134 °C
RTI StrUL 74680.0 °C
RTIUL 74680.0 °C
Linear coefficient of thermal expansionMD:-40到40°CASTME8311.1E-04 cm/cm/°C
TD：-40到40°CASTME8311.2E-04 cm/cm/°C
TD:-40到40°CASTME8311.2E-04 cm/cm/°C
vicatASTM D15255137 °C
RTI ImpUL 74680.0 °C
Heat distortion temperature1.8MPa,未退火,3.20mm，HDTASTM D648117 °C
RTI ElecUL 74680.0 °C