Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133 | 5.3 g/10min |
| Melt volume flow rate | | ISO 1133 | 5.00 cm3/10min |
| Shrinkage rate | | ISO 294-4 | 0.40 % |
| Shrinkage rate | | ISO 294-4 | 0.20 % |
| Water absorption rate | | ISO 62 | 0.70 % |
| Water absorption rate | | ISO 62 | 0.20 % |
| MediumDensity | | | 1.02 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 868 | 38 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Flammability level | | IEC 60695-11-10,-20 | HB |
| Limiting Oxygen Index | | ISO 4589-2 | 20 % |
| FMVSS flammability | | FMVSS302 | SE |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527-2 | 4.10 Mpa |
| tensile strength | | ISO 527-2 | 7.30 Mpa |
| Tensile modulus | | ISO 527-2 | 56.0 Mpa |
| tensile strength | | ISO 527-2 | 26.0 Mpa |
| tensile strength | | ISO 527-2 | 2.40 Mpa |
| Tensile strain | | ISO 527-2 | >300 % |
| Tensile creep modulus | | ISO 899-1 | 50.0 Mpa |
| Tensile creep modulus | | ISO 899-1 | 40.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 8256/1 | 230 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | NoBreak |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | NoBreak |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tear strength | | ISO 34-1 | 110 kN/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| relative permittivity | | IEC 60250 | 5.20 |
| relative permittivity | | IEC 60250 | 4.70 |
| Dissipation Factor | | IEC 60250 | 0.011 |
| Dissipation Factor | | IEC 60250 | 0.053 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Surface Resistivity | | IEC 60093 | 2E+14 ohms |
| Volume resistivity | | IEC 60093 | 7E+12 ohms·cm |
| dielectric strength | | IEC 60243-1 | 18 KV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | ISO 11357-2 | -50.0 °C |
| melting temperature | | ISO 11357-3 | 150 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 2.2E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 2.2E-04 cm/cm/°C |
| Effective thermal diffusivity coefficient | | | 5.44E-08 m²/s |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.