TPEE 4053FG NC010 DUPONT LUXEMBOURG
BEXLOY®
Automotive Applications、Fitness equipment、electrical equipment、Non specific food applica
Thermal stability、Aging resistance、UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT LUXEMBOURG/4053FG NC010 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | NoBreak |
| Tensile impact strength | 23°C | ISO8256/1 | 230 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | NoBreak |
| hardness | Test Condition | Test Method | DUPONT LUXEMBOURG/4053FG NC010 |
|---|---|---|---|
| 邵氏D,15秒 | ISO868 | 38 |
| Mechanical properties | Test Condition | Test Method | DUPONT LUXEMBOURG/4053FG NC010 |
|---|---|---|---|
| Tensile stress | 断裂 | ISO527-2 | 26.0 Mpa |
| 10%应变 | ISO527-2 | 4.10 Mpa | |
| TensileCreepModule | 1hr | ISO899-1 | 50.0 Mpa |
| Tensile stress | 50%应变 | ISO527-2 | 7.30 Mpa |
| Tensile modulus | ISO527-2 | 56.0 Mpa | |
| Tensile stress | 5.0%应变 | ISO527-2 | 2.40 Mpa |
| Tensile creep modulus | 1000hr | ISO899-1 | 40.0 Mpa |
| Tensile strain | 断裂 | ISO527-2 | >300 % |
| Electrical performance | Test Condition | Test Method | DUPONT LUXEMBOURG/4053FG NC010 |
|---|---|---|---|
| 100Hz | IEC60250 | 5.20 | |
| Surface Resistivity | IEC60093 | 2E+14 ohms | |
| CTI | IEC60112 | 600 V | |
| Dissipation Factor | 100Hz | IEC60250 | 0.011 |
| Volume resistivity | IEC60093 | 7E+12 ohms·cm | |
| Dissipation Factor | 1MHz | IEC60250 | 0.053 |
| dielectric strength | IEC60243-1 | 18 KV/mm | |
| 1MHz | IEC60250 | 4.70 |
| flammability | Test Condition | Test Method | DUPONT LUXEMBOURG/4053FG NC010 |
|---|---|---|---|
| Flammability level | 1.5mm | IEC60695-11-10,-20 | HB |
| FMVSS flammability | FMVSS302 | SE | |
| UL flame retardant rating | 1.5mm | UL94 | HB |
| Limiting Oxygen Index | ISO4589-2 | 20 % |
| physical property | Test Condition | Test Method | DUPONT LUXEMBOURG/4053FG NC010 |
|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 0.40 % |
| Water absorption rate | 饱和,23°C,2.00mm | ISO62 | 0.70 % |
| melt mass-flow rate | 190°C/2.16kg | ISO1133 | 5.3 g/10min |
| Melt volume flow rate | 190°C/2.16kg | ISO1133 | 5.00 cm3/10min |
| Shrinkage rate | MD | ISO294-4 | 0.20 % |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO62 | 0.20 % |
| MediumDensity | 1.02 g/cm³ |
| elastomer | Test Condition | Test Method | DUPONT LUXEMBOURG/4053FG NC010 |
|---|---|---|---|
| TearStrength-Flow | ISO34-1 | 110 kN/m |
| Thermal performance | Test Condition | Test Method | DUPONT LUXEMBOURG/4053FG NC010 |
|---|---|---|---|
| TD | ISO11359-2 | 2.2E-04 cm/cm/°C | |
| EffectiveThermal Diffusivity | 5.44E-08 m²/s | ||
| Glass transition temperature 2 | ISO11357-2 | -50.0 °C | |
| melting temperature | ISO11357-3 | 150 °C | |
| MD | ISO11359-2 | 2.2E-04 cm/cm/°C |