PBT VALOX™ 310SEO-1001 SABIC INNOVATIVE THAILAND
26
- Properties:Flame retardant
- Usages:Industrial applicationsElectrical fieldElectronic fieldSwitch panelShell
- Certificates:UL
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Specific volume | ASTM D792 | 0.710 cm³/g | |
| melt mass-flow rate | ASTM D1238 | 8.6 g/10 min | |
| Molten Volume Flow Rate (MVR) | ISO 1133 | 8.00 cm3/10min | |
| Shrinkage rate | 内部方法 | 1.1 到 1.8 % | |
| 内部方法 | 0.90 到 1.6 % | ||
| 内部方法 | 1.5 到 2.3 % | ||
| 内部方法 | 1.5 到 2.3 % | ||
| 内部方法 | 0.90 到 1.9 % | ||
| 内部方法 | 1.0 到 1.7 % | ||
| 内部方法 | 1.6 到 2.4 % | ||
| Water absorption rate | ISO 62 | 0.36 % | |
| ISO 62 | 0.080 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 120 | |
| Ball Indentation Hardness | ISO 2039-1 | 105 Mpa |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 | |
| UL 94 | 5VA | ||
| Burning wire flammability index | IEC 60695-2-12 | 960 °C | |
| Limiting Oxygen Index | ISO 4589-2 | 30 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2820 Mpa | |
| ISO 527-2/1 | 2800 Mpa | ||
| tensile strength | ASTM D638 | 58.0 Mpa | |
| ISO 527-2/50 | 58.0 Mpa | ||
| ASTM D638 | 52.0 Mpa | ||
| ISO 527-2/50 | 40.0 Mpa | ||
| elongation | ASTM D638 | 5.0 % | |
| ISO 527-2/50 | 5.0 % | ||
| ASTM D638 | 18 % | ||
| ISO 527-2/50 | 18 % | ||
| Flexural modulus | ASTM D790 | 2620 Mpa | |
| ISO 178 | 2600 Mpa | ||
| Bending stress | ISO 178 | 90.0 Mpa | |
| ASTM D790 | 101 Mpa | ||
| Taber Abrasion Resistance | 内部方法 | 19.0 mg |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Simple supported beam without notch impact strength 8 | ISO 179/1eU | 无断裂 | |
| ISO 179/1eU | 无断裂 | ||
| Unnotched Izod Impact Strength | ASTM D4812, ISO 180/1U | 无断裂 | |
| ISO 180/1U | 无断裂 | ||
| Dart impact equipped with measuring instruments | ASTM D3763 | 200 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | > 1.0E+15 ohms | |
| Volume resistivity | IEC 60093 | > 1.0E+15 ohms·cm | |
| dielectric strength | ASTM D149 | 24 KV/mm | |
| ASTM D149 | 18 KV/mm | ||
| IEC 60243-1 | 35 KV/mm | ||
| IEC 60243-1 | 18 KV/mm | ||
| IEC 60243-1 | 25 KV/mm | ||
| IEC 60243-1 | 17 KV/mm | ||
| Relative Permittivity | IEC 60250 | 2.90 | |
| IEC 60250 | 2.90 | ||
| IEC 60250 | 3.10 | ||
| IEC 60250 | 2.80 | ||
| Dissipation Factor | IEC 60250 | 1.0E-3 | |
| IEC 60250 | 1.0E-3 | ||
| IEC 60250 | 2.0E-3 | ||
| IEC 60250 | 0.013 | ||
| Arc resistance 13 | ASTM D495 | PLC 6 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 3 | |
| CTI | IEC 60112 | 175 V | |
| IEC 60112 | 100 V | ||
| High arc combustion index (HAI) | UL 746 | PLC 0 | |
| High Voltage Arc Resistance Index (HVAR) (PLC) | UL 746 | PLC 6 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 4 | |
| Hot wire ignition (HWI) | UL 746 | PLC 2 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 120 °C | ||
| drying time | 3.0 到 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 40 到 80 % | ||
| Temperature at the rear of the barrel | 230 到 250 °C | ||
| Temperature in the middle of the barrel | 240 到 255 °C | ||
| Temperature at the front of the material cylinder | 245 到 260 °C | ||
| Nozzle Temperature | 240 到 255 °C | ||
| Processing (melt) temperature | 245 到 260 °C | ||
| Temperature | 50 到 75 °C | ||
| Back pressure | 0.300 到 0.700 Mpa | ||
| screw speed | 50 到 100 rpm | ||
| Exhaust hole depth | 0.013 到 0.025 mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Thermal deformation temperature under load | ASTM D648 | 162 °C | |
| ISO 75-2/Be | 150 °C | ||
| ASTM D648 | 74.0 °C | ||
| ASTM D648 | 71.0 °C | ||
| ISO 75-2/Ae | 60.0 °C | ||
| ISO 75-2/Af | 73.0 °C | ||
| vicat | ASTM D152511, ISO 306/B50, ISO 306/B120 | 170 °C | |
| ISO 306/A50 | 212 °C | ||
| Ball Pressure Test | IEC 60695-10-2 | 通过 | |
| Linear thermal expansion coefficient | ASTM E831 | 7.9E-5 cm/cm/°C | |
| ASTM E831 | 1.3E-4 cm/cm/°C | ||
| ISO 11359-2 | 7.6E-5 cm/cm/°C | ||
| ISO 11359-2 | 1.0E-4 cm/cm/°C | ||
| ASTM E831 | 7.9E-5 cm/cm/°C | ||
| ISO 11359-2 | 7.3E-5 cm/cm/°C | ||
| ISO 11359-2 | 1.0E-4 cm/cm/°C | ||
| thermal conductivity | ISO 8302 | 0.24 W/m/K | |
| RTI Elec | UL 746 | 120 °C | |
| RTI Imp | UL 746 | 120 °C | |
| RTI | UL 746 | 140 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.