Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 310SEO-1001 SABIC INNOVATIVE THAILAND
VALOX™
Industrial applications、Electrical field、Electronic field、Switch panel、Shell
Flame retardant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/310SEO-1001 |
|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C, Total Energy | ASTM D3763 | 200 J |
| Simple supported beam without notch impact strength 8 | -30°C | ISO 179/1eU | 无断裂 |
| Unnotched Izod Impact Strength | -30°C 9 | ISO 180/1U | 无断裂 |
| Simple supported beam without notch impact strength 8 | 23°C | ISO 179/1eU | 无断裂 |
| Unnotched Izod Impact Strength | 23°C | ASTM D4812, ISO 180/1U | 无断裂 |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/310SEO-1001 |
|---|---|---|---|
| Ball Indentation Hardness | H 358/30 | ISO 2039-1 | 105 Mpa |
| Rockwell hardness | R 计秤 | ISO 2039-2 | 120 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/310SEO-1001 |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/50 | 58.0 Mpa |
| Bending stress | -- 6, 7 | ISO 178 | 90.0 Mpa |
| elongation | 断裂 | ISO 527-2/50 | 18 % |
| Flexural modulus | -- 6 | ISO 178 | 2600 Mpa |
| elongation | 屈服 4 | ASTM D638 | 5.0 % |
| Bending stress | 屈服, 50.0 mm 跨距 5 | ASTM D790 | 101 Mpa |
| Tensile modulus | -- 3 | ASTM D638 | 2820 Mpa |
| tensile strength | 屈服 4 | ASTM D638 | 58.0 Mpa |
| 断裂 | ISO 527-2/50 | 40.0 Mpa | |
| elongation | 屈服 | ISO 527-2/50 | 5.0 % |
| Flexural modulus | 50.0 mm 跨距 5 | ASTM D790 | 2620 Mpa |
| tensile strength | 断裂 4 | ASTM D638 | 52.0 Mpa |
| Taber Abrasion Resistance | 1000 Cycles, 1000 g, CS-17 转轮 | 内部方法 | 19.0 mg |
| Tensile modulus | -- | ISO 527-2/1 | 2800 Mpa |
| elongation | 断裂 4 | ASTM D638 | 18 % |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/310SEO-1001 |
|---|---|---|---|
| dielectric strength | 1.60 mm, in Oil | ASTM D149 | 24 KV/mm |
| 0.800 mm, 在油中 | IEC 60243-1 | 35 KV/mm | |
| CTI | -- | IEC 60112 | 175 V |
| Relative Permittivity | 100 Hz | IEC 60250 | 3.10 |
| Dissipation Factor | 100 Hz | IEC 60250 | 2.0E-3 |
| Relative Permittivity | 60 Hz | IEC 60250 | 2.90 |
| Dissipation Factor | 50 Hz | IEC 60250 | 1.0E-3 |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 3 | |
| dielectric strength | 1.00 mm 12 | IEC 60243-1 | 18 KV/mm |
| High arc combustion index (HAI) | UL 746 | PLC 0 | |
| dielectric strength | 1.60 mm, 在油中 | IEC 60243-1 | 25 KV/mm |
| Dissipation Factor | 1 MHz | IEC 60250 | 0.013 |
| Volume resistivity | IEC 60093 | > 1.0E+15 ohms·cm | |
| Arc resistance 13 | ASTM D495 | PLC 6 | |
| CTI | 解决方案 B | IEC 60112 | 100 V |
| Relative Permittivity | 1 MHz | IEC 60250 | 2.80 |
| Dissipation Factor | 60 Hz | IEC 60250 | 1.0E-3 |
| Hot wire ignition (HWI) | UL 746 | PLC 2 | |
| dielectric strength | 3.20 mm, in Air | ASTM D149 | 18 KV/mm |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 4 | |
| Surface Resistivity | IEC 60093 | > 1.0E+15 ohms | |
| dielectric strength | 3.20 mm, 在油中 | IEC 60243-1 | 17 KV/mm |
| High Voltage Arc Resistance Index (HVAR) (PLC) | UL 746 | PLC 6 | |
| Relative Permittivity | 50 Hz | IEC 60250 | 2.90 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/310SEO-1001 |
|---|---|---|---|
| UL flame retardant rating | 0.71 mm | UL 94 | V-0 |
| 3.0 mm | UL 94 | 5VA | |
| Burning wire flammability index | 1.0 mm | IEC 60695-2-12 | 960 °C |
| Limiting Oxygen Index | ISO 4589-2 | 30 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/310SEO-1001 |
|---|---|---|---|
| melt mass-flow rate | 250°C/2.16 kg | ASTM D1238 | 8.6 g/10 min |
| Shrinkage rate | 流动 : 2.30 到 4.60 mm | 内部方法 | 1.5 到 2.3 % |
| 横向流动 : 0.750 到 2.30 mm | 内部方法 | 1.0 到 1.7 % | |
| 横向流动 2 | 内部方法 | 0.90 到 1.9 % | |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.080 % |
| Shrinkage rate | 流动 2 | 内部方法 | 1.1 到 1.8 % |
| 横向流动 : 2.30 到 4.60 mm | 内部方法 | 1.6 到 2.4 % | |
| Specific volume | ASTM D792 | 0.710 cm³/g | |
| Shrinkage rate | 流动 : 0.750 到 2.30 mm | 内部方法 | 0.90 到 1.6 % |
| Molten Volume Flow Rate (MVR) | 250°C/2.16 kg | ISO 1133 | 8.00 cm3/10min |
| Shrinkage rate | 流动 : 3.20 mm | 内部方法 | 1.5 到 2.3 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.36 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/310SEO-1001 |
|---|---|---|---|
| vicat | -- | ASTM D152511, ISO 306/B50, ISO 306/B120 | 170 °C |
| Linear thermal expansion coefficient | 流动 : -40 到 40°C | ISO 11359-2 | 7.6E-5 cm/cm/°C |
| Thermal deformation temperature under load | 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 10 | ISO 75-2/Be | 150 °C |
| Linear thermal expansion coefficient | 流动 : 23 到 60°C | ISO 11359-2 | 1.0E-4 cm/cm/°C |
| 流动 : -40 到 40°C | ASTM E831 | 7.9E-5 cm/cm/°C | |
| Thermal deformation temperature under load | 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 71.0 °C |
| Linear thermal expansion coefficient | 横向 : 23 到 60°C | ISO 11359-2 | 1.0E-4 cm/cm/°C |
| 横向 : -40°C | ISO 11359-2 | 7.3E-5 cm/cm/°C | |
| RTI | UL 746 | 140 °C | |
| Thermal deformation temperature under load | 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 10 | ISO 75-2/Ae | 60.0 °C |
| thermal conductivity | ISO 8302 | 0.24 W/m/K | |
| Linear thermal expansion coefficient | 流动 : 60 到 138°C | ASTM E831 | 1.3E-4 cm/cm/°C |
| 横向 : -40 到 40°C | ASTM E831 | 7.9E-5 cm/cm/°C | |
| Thermal deformation temperature under load | 0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 162 °C |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 74.0 °C | |
| vicat | -- | ISO 306/A50 | 212 °C |
| Ball Pressure Test | 123 到 127°C | IEC 60695-10-2 | 通过 |
| Thermal deformation temperature under load | 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 9 | ISO 75-2/Af | 73.0 °C |
| RTI Imp | UL 746 | 120 °C | |
| RTI Elec | UL 746 | 120 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/310SEO-1001 |
|---|---|---|---|
| Nozzle Temperature | 240 到 255 °C | ||
| Processing (melt) temperature | 245 到 260 °C | ||
| drying temperature | 120 °C | ||
| Exhaust hole depth | 0.013 到 0.025 mm | ||
| Temperature at the front of the material cylinder | 245 到 260 °C | ||
| Suggested maximum moisture content | 0.020 % | ||
| Temperature in the middle of the barrel | 240 到 255 °C | ||
| Temperature | 50 到 75 °C | ||
| screw speed | 50 到 100 rpm | ||
| Temperature at the rear of the barrel | 230 到 250 °C | ||
| Back pressure | 0.300 到 0.700 Mpa | ||
| drying time | 3.0 到 4.0 hr | ||
| Suggested injection volume | 40 到 80 % |