Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.26to1.30 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 868 | 84to88 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Limiting Oxygen Index | | ISO 4589-2 | 26to29 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Resistance Against Saponification | | HD22.10S1 | <200 mgKOH/g |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ISO 527-2 | 32.4to39.6 MPa |
| Tensile strain | Break | ISO 527-2 | 580to700 % |
| wear resistance | | DIN 53516 | 37.0to47.0 mm³ |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tear strength | | DIN 53515 | 77.0to87.0 kN/m |
| aging | Test Condition | Test Method | Test Result |
|---|
| Change rate of ultimate elongation in air | | UL 1581 | <-30 % |
| Change rate of ultimate elongation in air | | UL 1581 | <-30 % |
| Change rate of tensile strength in air | | UL 1581 | <-30 % |
| Change rate of ultimate elongation in air | | UL 1581 | <-30 % |
| Change rate of tensile strength in air | | UL 1581 | <-30 % |
| Change rate of tensile strength in air | | UL 1581 | <-30 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | >5.0E+13 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| brittle temperature | | ISO 458 | -43.0--39.0 °C |
| thermal stability | | ISO R182 | >80 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.