PBT/F/PTFE LNP™ LUBRICOMP™ WFL-4036 NAT
48
- Properties:High temperature resistanAging resistance
- Usages:Automotive componentsElectrical field
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 0.10-0.30 % | |
| ISO 294-4 | 0.50-1.0 % | ||
| ASTM D955 | 0.50-1.0 % | ||
| ASTM D955 | 0.10-0.30 % | ||
| Water absorption rate | ISO 62 | 0.040 % | |
| ASTM D570 | 0.040 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 2.61 J | |
| Dart impact | ASTM D3763 | 13.7 J | |
| Suspended wall beam without notch impact strength | ISO 180/1U | 43 kJ/m² | |
| Impact strength of cantilever beam gap | ISO 180/1A | 9.2 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | ISO 178 | 187 Mpa | |
| ASTM D790 | 193 Mpa | ||
| Flexural modulus | ISO 178 | 10000 Mpa | |
| ASTM D790 | 10200 Mpa | ||
| Tensile strain | ISO 527-2 | 2.2 % | |
| elongation | ASTM D638 | 2.3 % | |
| tensile strength | ISO 527-2 | 118 Mpa | |
| ASTM D638 | 118 Mpa | ||
| Tensile modulus | ISO 527-2/1 | 10600 Mpa | |
| ASTM D638 | 10300 Mpa | ||
| Wear factor | ASTM D3702Modified | 42.0 10^-10in^5-min/ft-lb-hr | |
| coefficient of friction | ASTM D3702Modified | 0.41 | |
| ASTM D3702Modified | 0.57 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/Af | 214 °C | |
| Linear coefficient of thermal expansion | ASTME831 | 3.9E-05 cm/cm/°C | |
| ISO 11359-2 | 3.9E-05 cm/cm/°C | ||
| Heat distortion temperature | ASTM D648 | 218 °C | |
| Linear coefficient of thermal expansion | ASTME831 | 6.7E-05 cm/cm/°C | |
| ISO 11359-2 | 6.7E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.