Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT/F/PTFE WFL-4036 NAT SABIC INNOVATIVE US
LNP™ LUBRICOMP™ 
Automotive components、Electrical field
High temperature resistan、Aging resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE US/WFL-4036 NAT
Suspended wall beam without notch impact strength23°CISO 180/1U43 kJ/m²
Multi axis Instrumented Impact EnergyISO 6603-22.61 J
Impact strength of cantilever beam gap23°CISO 180/1A9.2 kJ/m²
Dart impact23°C,EnergyatPeakLoadASTM D376313.7 J
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/WFL-4036 NAT
Tensile modulusISO 527-2/110600 Mpa
bending strengthASTM D790193 Mpa
tensile strength 断裂ASTM D638118 Mpa
断裂ISO 527-2118 Mpa
Wear factorWasherASTM D3702Modified42.0 10^-10in^5-min/ft-lb-hr
Flexural modulusASTM D79010200 Mpa
Tensile modulusASTM D63810300 Mpa
elongation断裂ASTM D6382.3 %
bending strengthISO 178187 Mpa
coefficient of frictionStaticASTM D3702Modified0.41
Tensile strain断裂ISO 527-22.2 %
Flexural modulusISO 17810000 Mpa
coefficient of frictionDynamicASTM D3702Modified0.57
physical property Test ConditionTest MethodSABIC INNOVATIVE US/WFL-4036 NAT
Shrinkage rateMD:24小时ISO 294-40.10-0.30 %
MD：24小时ASTM D9550.10-0.30 %
Water absorption rate24hr,50%RHASTM D5700.040 %
平衡,23°C,50%RHISO 620.040 %
Shrinkage rateTD：24hrASTM D9550.50-1.0 %
TD:24小时ISO 294-40.50-1.0 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/WFL-4036 NAT
Linear coefficient of thermal expansionTD：-40到40°CASTME8316.7E-05 cm/cm/°C
TD：-40到40°CISO 11359-26.7E-05 cm/cm/°C
MD：-40到40°CASTME8313.9E-05 cm/cm/°C
MD：-40到40°CISO 11359-23.9E-05 cm/cm/°C
Heat distortion temperature1.8MPa,未退火,64.0mm跨距，HDTISO 75-2/Af214 °C
1.8MPa,未退火,3.20mm，HDTASTM D648218 °C