Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.04 g/cm³ |
| Water absorption rate | | ISO 62 | 0.70 % |
| Water absorption rate | | ISO 62 | 1.2 % |
| melt mass-flow rate | | ISO 1133 | 15 g/10min |
| melt mass-flow rate | | ISO 62 | 2.9 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Hardness (Shore A) | | ISO 868 | 77 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation at break | | ISO 527-2 | >=100 % |
| elongation at break | | ISO 527-2 | 4.1 % |
| Tensile modulus | | ISO 527-2 | - MPa |
| Tensile creep modulus | | ISO 899-1 | 2270 MPa |
| Tensile creep modulus | | ISO 899-1 | - MPa |
| bending strength | | ISO 178 | 67.0 MPa |
| bending strength | | ISO 178 | 75.0 MPa |
| Flexural modulus | | ISO 178 | 2100 MPa |
| Flexural modulus | | ISO 178 | 2300 MPa |
| Charpy Notched Impact Strength | | ISO 179/1eA | 17 kJ/m² |
| Charpy Notched Impact Strength | | ISO R527 | 2600 MPa |
| Charpy Notched Impact Strength | | ISO 179/Af | 12 kJ/m² |
| tensile strength | | ISO 527-2 | 51.5 MPa |
| tensile strength | | ISO 527-2 | 50.0 MPa |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL -94 | HB - |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC 60093 | 6E+15 Ω.cm |
| Surface Resistivity | | IEC 60093 | 2.5E+16 Ω.cm |
| dielectric strength | | IEC 60243-1 | 36.0 KV/mm |
| Dissipation Factor | | IEC 60250 | 0.025 |
| Dissipation Factor | | IEC 60250 | 0.017 |
| Dissipation Factor | | IEC 60250 | 0.032 1kHz |
| Dissipation Factor | | IEC 60112 | >=600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/Af | 80.0 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1.1E-04 cm/cm／°C |
| Heat distortion temperature | | ISO 75-2/Bf | 160 °C |
| vicat | | ISO 306/A50 | 165 °C |
| vicat | | ISO 306/B50 | 225 °C |
| vicat | Melting Temperature | ISO 11357-3 | 255 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 6.5E-05 cm/cm／°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.