PA66 Alloy Orgalloy® RS 6600 ARKEMA FRANCE
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | ARKEMA FRANCE/Orgalloy® RS 6600 |
|---|---|---|---|
| Hardness (Shore A) | ISO 868 | 77 |
| Electrical performance | Test Condition | Test Method | ARKEMA FRANCE/Orgalloy® RS 6600 |
|---|---|---|---|
| Dissipation Factor | IEC 60250 | 0.017 | |
| dielectric strength | 1.00mm | IEC 60243-1 | 36.0 KV/mm |
| Dissipation Factor | 相对漏电起痕指数 | IEC 60112 | >=600 V |
| IEC 60250 | 0.032 1kHz | ||
| Surface Resistivity | IEC 60093 | 2.5E+16 Ω.cm | |
| Volume resistivity | IEC 60093 | 6E+15 Ω.cm |
| Mechanical properties | Test Condition | Test Method | ARKEMA FRANCE/Orgalloy® RS 6600 |
|---|---|---|---|
| Charpy Notched Impact Strength | 弹性模量 | ISO R527 | 2600 MPa |
| elongation at break | 50mm/min，屈服，23°C | ISO 527-2 | 4.1 % |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 17 kJ/m² |
| tensile strength | 50mm/min，屈服，23°C | ISO 527-2 | 51.5 MPa |
| elongation at break | 50mm/min，23°C | ISO 527-2 | >=100 % |
| bending strength | 调节后50%RH和23°C | ISO 178 | 67.0 MPa |
| Flexural modulus | 调节后50%RH和23°C | ISO 178 | 2100 MPa |
| Tensile modulus | 1mm/min，23°C | ISO 527-2 | - MPa |
| Flexural modulus | 23°C | ISO 178 | 2300 MPa |
| Tensile creep modulus | 1Hr | ISO 899-1 | 2270 MPa |
| tensile strength | 23°C | ISO 527-2 | 50.0 MPa |
| Charpy Notched Impact Strength | 简支梁缺口冲击强度 | ISO 179/Af | 12 kJ/m² |
| Tensile creep modulus | 1000Hr | ISO 899-1 | - MPa |
| bending strength | 23°C | ISO 178 | 75.0 MPa |
| Flame retardant performance | Test Condition | Test Method | ARKEMA FRANCE/Orgalloy® RS 6600 |
|---|---|---|---|
| UL flame retardant rating | UL -94 | HB - |
| physical property | Test Condition | Test Method | ARKEMA FRANCE/Orgalloy® RS 6600 |
|---|---|---|---|
| Water absorption rate | (23°C,24hr) | ISO 62 | 0.70 % |
| density | ISO 1183 | 1.04 g/cm³ | |
| Water absorption rate | (23°C,50RH) | ISO 62 | 1.2 % |
| melt mass-flow rate | 吸水率 | ISO 62 | 2.9 % |
| 235℃/5.00Kg | ISO 1133 | 15 g/10min |
| Thermal performance | Test Condition | Test Method | ARKEMA FRANCE/Orgalloy® RS 6600 |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 80.0 °C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 1.1E-04 cm/cm／°C |
| MD | ISO 11359-2 | 6.5E-05 cm/cm／°C | |
| vicat | 50N | ISO 306/A50 | 165 °C |
| 10N | ISO 306/B50 | 225 °C | |
| 熔融温度 | ISO 11357-3 | 255 °C | |
| Heat distortion temperature | 0.45MPa未退火，HDT | ISO 75-2/Bf | 160 °C |