PA+PPO(PPE) Infino HT-8200G LOTTE KOREA
0
CompareTechnical Data Sheet
| 物理性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 收缩率 | TD:3.20mm | ISO2577 | 0.50to0.61 % |
| MD:3.20mm | ISO2577 | 0.40to0.49 % | |
| 密度 | ASTMD792 | 1.24 g/cm³ | |
| ISO1183 | 1.24 g/cm³ | ||
| 熔体质量流动速率 | 285°C/5.0kg | ASTMD1238 | 20 g/10min |
| 285°C/5.0kg | ISO1133 | 20 g/10min | |
| 收缩率 | MD：3.20mm | ASTMD955 | 0.40to0.49 % |
| TD：3.20mm | ASTMD955 | 0.50to0.61 % |
| 机械性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 拉伸模量 | ASTMD638 | 8400 MPa | |
| ISO527-2/50 | 8800 MPa | ||
| 抗张强度 | Yield | ASTMD638 | 140 MPa |
| 弯曲模量 | ISO178 | 11000 MPa | |
| 弯曲强度 | ASTMD790 | 240 MPa | |
| 弯曲应力 | ISO178 | 210 MPa | |
| 弯曲模量 | ASTMD790 | 5900 MPa | |
| 拉伸应力 | Yield | ISO527-2/50 | 159 MPa |
| 抗张强度 | Break | ASTMD638 | 140 MPa |
| 拉伸应力 | Break | ISO527-2/50 | 160 MPa |
| 伸长率 | Break | ASTMD638 | 3.0 % |
| 拉伸应变 | Break | ISO527-2/50 | 3.0 % |
| 硬度 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 洛氏硬度 | R-Scale | ASTMD785 | 117 |
| R-Scale | ISO2039-2 | 117 |
| 热性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| CharpyNotchedImpactStrength | 23°C | ISO179/1eA | 10 kJ/m² |
| 悬壁梁缺口冲击强度 | 23°C,3.18mm | ASTMD256 | 88 J/m |
| 23°C,6.35mm | ASTMD256 | 69 J/m | |
| 23°C | ISO180/1A | 10 kJ/m² | |
| 热变形温度 | 0.45MPa,未退火,6.40mm | ASTMD648 | 250 °C |
| 0.45MPa,Unannealed,4.00mm | ISO75-2/B | 254 °C | |
| 1.8MPa,未退火,6.40mm | ASTMD648 | 231 °C | |
| 1.8MPa,Unannealed,4.00mm | ISO75-2/A | 234 °C | |
| 维卡软化温度 | ISO306/B50 | 248 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.