PA+PPO(PPE) Infino HT-8200G LOTTE KOREA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodLOTTE KOREA/Infino HT-8200G
Charpy Notched Impact Strength23°CISO 179/1eA10 kJ/m²
Impact strength of cantilever beam gap23°C,6.35mmASTM D25669 J/m
23°CISO 180/1A10 kJ/m²
23°C,3.18mmASTM D25688 J/m
hardnessTest ConditionTest MethodLOTTE KOREA/Infino HT-8200G
Rockwell hardnessR级ISO 2039-2117
R级ASTM D785117
Mechanical propertiesTest ConditionTest MethodLOTTE KOREA/Infino HT-8200G
elongation断裂ASTM D6383.0 %
Tensile modulusASTM D6388400 MPa
Flexural modulusASTM D7905900 MPa
tensile strength 断裂ASTM D638140 MPa
Tensile modulusISO 527-2/508800 MPa
tensile strength 屈服ASTM D638140 MPa
Flexural modulusISO 17811000 MPa
bending strengthASTM D790240 MPa
Tensile strain断裂ISO 527-2/503.0 %
bending strengthISO 178210 MPa
tensile strength 屈服ISO 527-2/50159 MPa
断裂ISO 527-2/50160 MPa
physical property Test ConditionTest MethodLOTTE KOREA/Infino HT-8200G
Shrinkage rateMD：3.20mmASTM D9550.40to0.49 %
TD:3.20mmISO 25770.50to0.61 %
TD：3.20mmASTM D9550.50to0.61 %
densityASTM D7921.24 g/cm³
ISO 11831.24 g/cm³
melt mass-flow rate285°C/5.0kgISO 113320 g/10min
285°C/5.0kgASTM D123820 g/10min
Shrinkage rateMD:3.20mmISO 25770.40to0.49 %
Thermal performanceTest ConditionTest MethodLOTTE KOREA/Infino HT-8200G
Heat distortion temperature1.8MPa,Unannealed,4.00mm，HDTISO 75-2/A234 °C
1.8MPa,未退火,6.40mm，HDTASTM D648231 °C
0.45MPa,Unannealed,4.00mm，HDTISO 75-2/B254 °C
vicatISO 306/B50248 °C
Heat distortion temperature0.45MPa,未退火,6.40mm，HDTASTM D648250 °C