Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 171 | 3.5 |
| Shrinkage rate | | ISO 2577 | 0.62 % |
| Shrinkage rate | | ISO 2577 | 0.58 % |
| Water absorption rate | | ISO 62 | 13.0 mg |
| Water absorption rate | | DIN 53472 | 70.0 mg |
| Water absorption rate | | ISO 62 | 50.0 mg |
| density | | ISO 1183 | 1.52 g/cm³ |
| Apparent density | | ISO 60 | 0.44 g/cm³ |
| Shrinkage rate | | ISO 2577 | 0.85 % |
| Shrinkage rate | | ISO 2577 | 1.1 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Limiting Oxygen Index | | ISO 4589-2 | 44 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ISO 178 | 119 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180/C | 2.2 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180 | 9.8 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | IEC 60243-1 | 6.1 kV/mm |
| dielectric strength | | IEC 60243-1 | 8.5 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60167 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/Ae | 186 °C |
| Martin's heat-resistant temperature | | DIN 43458 | 145 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.