Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D955 | 0.15 % |
| Shrinkage rate | | ASTM D955 | 0.17 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Burning wire flammability index | | IEC 60695-2-12 | 850650 °C |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 825 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| --1 | | ASTM D638 | 10800 Mpa |
| fracture | | ASTM D638 | 54.0 Mpa |
| fracture | | ISO 527-2/5 | 75.0 Mpa |
| fracture | | ASTM D638 | 1.0 % |
| fracture | | ISO 527-2/5 | 0.90 % |
| 50.0mm span | | ASTM D790 | 12400 Mpa |
| --5 | | ISO 178 | 14000 Mpa |
| --6 | | ISO 178 | 90.0 Mpa |
| Fracture, 50.0mm span | | ASTM D790 | 78.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| 23°C | | ASTM D256 | 26 J/m |
| 23°C | | ISO 180/1A | 3.0 kJ/m² |
| 23°C | | ASTM D4812 | 150 J/m |
| 23°C | | ISO 180/1U | 8.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTM D257 | 3E+05 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Flow: -40 to 40 ° C | | ASTME831 | 1.6E-05 cm/cm/°C |
| Flow: -30 to 80 ° C | | ISO 11359-2 | 1.4E-05 cm/cm/°C |
| Flow: 23 to 80 ° C | | ISO 11359-2 | 1.6E-05 cm/cm/°C |
| Horizontal: -40 to 40 ° C | | ASTME831 | 3.6E-05 cm/cm/°C |
| Horizontal: -30 to 80 ° C | | ISO 11359-2 | 4E-05 cm/cm/°C |
| Horizontal: 23 to 80 ° C | | ISO 11359-2 | 4.8E-05 cm/cm/°C |
| --11 | | ASTM D790/ISO 178 | 3.5 W/m/K |
| --12 | | ASTM D790/ISO 178 | 15 W/m/K |
| --13 | | ISO 22007-2 | 1.5 W/m/K |
| --14 | | ISO 22007-2 | 18 W/m/K |
| 1.8MPa, Unanealed, 3.20mm | | ASTM D648 | 186 °C |
| 1.8MPa, Unanealed, 64.0mm span | | ISO 75-2/Af | 200 °C |
| ball-indentation hardness | | IEC 60695-10-2 | Pass |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.