TPU-Capro IROGRAN® A 95 K 4640
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt volume flow rate | 5.00to10.0 cm³/10min | ||
| Shrinkage rate | ASTMD972 | 0.80 % | |
| density | ASTMD792 | 1.19 g/cm³ | |
| DIN53479 | 1.19 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ASTMD2240 | 95 | ||
| DIN53505 | 45 | ||
| ASTMD2240 | 45 | ||
| DIN53505 | 95 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile strength- | ASTMD412 | 6.69 MPa | |
| tensile strength | DIN53504 | 7.00 MPa | |
| Abrasion | ASTMD395 | 29 mm³ | |
| DIN53516 | 30 mm³ |
| elastomer | Test Condition | Test Method | Test Result |
|---|---|---|---|
| compression set | DIN53517 | 25 % | |
| DIN53517 | 38 % | ||
| ASTMD395 | 14 % | ||
| ASTMD395 | 25 % | ||
| ASTMD395 | 33 % | ||
| ASTMD395 | 38 % | ||
| DIN53517 | 14 % | ||
| DIN53517 | 23 % | ||
| tear strength | DIN53515 | 90 kN/m | |
| Tensile stress | ASTMD412 | 8.62 MPa | |
| DIN53504 | 9.00 MPa | ||
| ASTMD412 | 10.8 MPa | ||
| DIN53504 | 11.5 MPa | ||
| tensile strength | ASTMD412 | 14.0 MPa | |
| DIN53504 | 14.2 MPa | ||
| Tensile stress | ASTMD412 | 18.9 MPa | |
| DIN53504 | 20.4 MPa | ||
| tensile strength | Break | ASTMD412 | 37.2 MPa |
| Tensile stress | Break | DIN53504 | 53.0 MPa |
| elongation | Break | ASTMD412 | 570 % |
| Break | DIN53504 | 530 % | |
| tear strength | ASTMD624 | 126 kN/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | DIN53372 | 165 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.