Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 0.960 g/cm³ |
| Water absorption rate | | ISO62 | 0.010 % |
| molecular weight | | | 500000 g/mol |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO868 | 66 |
| | ISO868 | 64 |
| | ISO2039-1 | 45.0 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Limiting Oxygen Index | | ISO4589-2 | <20 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Relative Weight Loss | | 内部方法 | 350 |
| Relative Weight Loss | | 内部方法 | 1200 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | 内部方法 | >25 kJ/m² |
| Charpy Notched Impact Strength | Partial Break | ISO179/1eA | 110 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 无断裂 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| compression stress | | ISO604/1 | 9.00 MPa |
| compression stress | | ISO604/1 | 15.0 MPa |
| compression stress | | ISO604/1 | 23.0 MPa |
| Tensile modulus | | ISO527-2/1B/1 | 1350 MPa |
| Tensile stress | Yield | ISO527-2/1B/50 | 28.0 MPa |
| Tensile strain | Yield | ISO527-2/1B/50 | 10 % |
| Nominal tensile fracture strain | | ISO527-2/1B/50 | >50 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| | IEC60250 | 2.40 |
| Dissipation Factor | | IEC60250 | 2E-04 |
| Dissipation Factor | | IEC60250 | 2E-04 |
| CTI | | IEC60112 | 600 V |
| dielectric strength | | IEC60243-1 | 45 kV/mm |
| | IEC60250 | 2.40 |
| Surface Resistivity | | IEC60093 | >1.0E+13 ohms |
| Volume resistivity | | IEC60093 | >1.0E+14 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 44.0 °C |
| Continuous use temperature | | | 80.0 °C |
| Continuous use temperature | | | 120 °C |
| vicat | | ISO306/B | 80.0 °C |
| melting temperature | | ISO11357-3 | 130到135 °C |
| | | 1.5E-04 cm/cm/°C |
| thermal conductivity | | | 0.40 W/m/K |
| Service Temperature Minimum | | | -100 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.