Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
HDPE Quadrant EPP CESTILENE HD 500 Mitsubishi Chemical Advanced Materials
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP CESTILENE HD 500 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1eU | 无断裂 | |
| Charpy Notched Impact Strength | 局部断裂 | ISO 179/1eA | 110 kJ/m² |
| --2 | 内部方法 | >25 kJ/m² |
| hardness | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP CESTILENE HD 500 |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 45.0 MPa | |
| Shore hardness | 邵氏D,3秒 | ISO 868 | 66 |
| 邵氏D,15秒 | ISO 868 | 64 |
| Supplementary Information | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP CESTILENE HD 500 |
|---|---|---|---|
| Relative Weight Loss | --6 | 内部方法 | 1200 |
| --5 | 内部方法 | 350 |
| Mechanical properties | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP CESTILENE HD 500 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1B/1 | 1350 MPa | |
| Nominal tensile fracture strain | ISO 527-2/1B/50 | >50 % | |
| Tensile strain | 屈服 | ISO 527-2/1B/50 | 10 % |
| tensile strength | 屈服 | ISO 527-2/1B/50 | 28.0 MPa |
| compression stress | 1%应变 | ISO 604/1 | 9.00 MPa |
| 2%应变 | ISO 604/1 | 15.0 MPa | |
| 5%应变 | ISO 604/1 | 23.0 MPa |
| Electrical performance | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP CESTILENE HD 500 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| Volume resistivity | IEC 60093 | >1.0E+14 ohms·cm | |
| Dissipation Factor | 100Hz | IEC 60250 | 2E-04 |
| relative permittivity | 100Hz | IEC 60250 | 2.40 |
| dielectric strength | 1.00mm,在油中 | IEC 60243-1 | 45 kV/mm |
| relative permittivity | 1MHz | IEC 60250 | 2.40 |
| Surface Resistivity | IEC 60093 | >1.0E+13 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 2E-04 |
| flammability | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP CESTILENE HD 500 |
|---|---|---|---|
| Limiting Oxygen Index | ISO 4589-2 | <20 % | |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP CESTILENE HD 500 |
|---|---|---|---|
| molecular weight distribution | 500000 g/mol | ||
| Water absorption rate | 饱和,23°C,1.00mm | ISO 62 | 0.010 % |
| density | ISO 1183 | 0.960 g/cm³ |
| Thermal performance | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP CESTILENE HD 500 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 130to135 °C | |
| vicat | ISO 306/B | 80.0 °C | |
| Minimum operating temperature | -100 °C | ||
| thermal conductivity | 23°C | 0.40 W/m/K | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 44.0 °C |
| Continuous use temperature | --3 | 80.0 °C | |
| --4 | 120 °C | ||
| Linear coefficient of thermal expansion | MD：23到100°C | 1.5E-04 cm/cm/°C |