AS(SAN) PN-107L125 TAIWAN CHIMEI

210

Form：Granules | Grade：Injection grade

Properties:

transparentHigh transparencyInjection moldingoneDry the material at 75-80twoThe temperature of the inthreeThe injection pressure iscm2fourMaintain a pressure of 40cm2fiveBack pressure is 5-15kgcm2sixThe mold temperature is bsevenDo not leave the hot melt

Typical Applications:

chipcontainerHousehold goodsFood containersseal potCosmetics boxes etc

Supplier(1)

Product Description

Certificates(2)

Datasheet

Alternative Model(1)

Product Description

Typical Applications:	chip \| container \| Household goods \| Food containers \| seal pot \| Cosmetics boxes \| etc
Properties:	transparent \| High transparency \| Injection molding \| one \| Dry the material at 75-80 \| two \| The temperature of the in \| three \| The injection pressure is \| cm<sup>2< \| sup> \| four \| Maintain a pressure of 40 \| cm<sup>2< \| sup> \| five \| Back pressure is 5-15kg \| cm<sup>2< \| sup> \| six \| The mold temperature is b \| seven \| Do not leave the hot melt

Certificates

MSDS

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus		ASTM D790	3450	Mpa
Bending modulus	Bending modulus		ISO 178	2600	Mpa
bending strength		ASTM D790	88.3	Mpa
bending strength	bending strength		ISO 178	89.0	Mpa
tensile strength	Yield	ASTM D638	60.7	Mpa
	tensile strength	Yield	ISO 527-2/50	65.0	Mpa
	tensile strength	tensile strength	Break	ISO 527-2/50	65.0	Mpa
elongation	Break	ASTM D638	5.0	%
Tensile strain	Break	ISO 527-2/50	4.0	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	99.0	°C
Vicat softening temperature		ASTM D15256	104	°C
	Vicat softening temperature	--	ISO 306/A50	104	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	101	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	3.6E-5to3.8E-5	cm/cm/°C
Hot deformation temperature	Annealed	ASTM D648	100	°C
	Hot deformation temperature	Unannealed	ASTM D648	90	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	88.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	200°C/5.0kg	ASTM D1238	5.0	g/10min
Melt Volume Flow Rate (MVR)	220°C/10.0kg	ISO 1133	58.0	cm3/10min
Shrinkage rate		ISO 294-4	0.20-0.70	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Scale	ASTM D785	83

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.