Material Comparison

Product Info

Product Name

Brand Name

Usages

Properties

Certificates

AS(SAN) PN-107L125 TAIWAN CHIMEI

KIBISAN®

chip、container、Household goods、Food containers、seal pot、Cosmetics boxes, etc

transparent、High transparency、Injection molding、one、Dry the material at 75-80、two、The temperature of the in、three、The injection pressure is、cm<sup>2<、sup>、four、Maintain a pressure of 40、cm<sup>2<、sup>、five、Back pressure is 5-15kg、cm<sup>2<、sup>、six、The mold temperature is b、seven、Do not leave the hot melt

MSDS

Plastic Datasheets

hardness	Test Condition	Test Method	TAIWAN CHIMEI/PN-107L125
Rockwell hardness	M级	ASTM D785	83

Mechanical properties	Test Condition	Test Method	TAIWAN CHIMEI/PN-107L125
tensile strength	屈服	ISO 527-2/50	65.0 Mpa
elongation	断裂	ASTM D638	5.0 %
bending strength		ISO 178	89.0 Mpa
Flexural modulus		ISO 178	2600 Mpa
bending strength		ASTM D790	88.3 Mpa
tensile strength	屈服	ASTM D638	60.7 Mpa
Tensile strain	断裂	ISO 527-2/50	4.0 %
Flexural modulus		ASTM D790	3450 Mpa
tensile strength	断裂	ISO 527-2/50	65.0 Mpa

flammability	Test Condition	Test Method	TAIWAN CHIMEI/PN-107L125
UL flame retardant rating	1.5mm	UL 94	HB

physical property	Test Condition	Test Method	TAIWAN CHIMEI/PN-107L125
melt mass-flow rate	200°C/5.0kg	ASTM D1238	5.0 g/10min
Shrinkage rate		ISO 294-4	0.20-0.70 %
Melt volume flow rate	220°C/10.0kg	ISO 1133	58.0 cm3/10min

Thermal performance	Test Condition	Test Method	TAIWAN CHIMEI/PN-107L125
vicat		ASTM D15256	104 °C
vicat		--	ISO 306/A50	104 °C
Heat distortion temperature	Unannealed，HDT	ASTM D648	90 °C
Heat distortion temperature		1.8MPa,退火，HDT	ISO 75-2/A	99.0 °C
vicat	--	ISO 306/B50	101 °C
Heat distortion temperature	1.8MPa,未退火，HDT	ISO 75-2/A	88.0 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	3.6E-5to3.8E-5 cm/cm/°C
Heat distortion temperature	Annealed，HDT	ASTM D648	100 °C