Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
density | | ASTM D792 | 1.20 g/cm³ |
melt mass-flow rate | | ASTM D1238 | 6.0 g/10min |
Shrinkage rate | | ASTM D955 | 0.50to0.70 % |
Water absorption rate | | ASTM D570 | 0.15 % |
Water absorption rate | | ASTM D570 | 0.32 % |
hardness | Test Condition | Test Method | Test Result |
---|
Rockwell hardness | | ASTM D785 | 73 |
Rockwell hardness | R-Scale | ASTM D785 | 118 |
flammability | Test Condition | Test Method | Test Result |
---|
UL flame retardant rating | | UL 94 | HB |
UL flame retardant rating | | UL 94 | V-2 |
UL flame retardant rating | | UL 94 | V-2 |
Limiting Oxygen Index | | ISO 4589-2 | 26 % |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
Tensile modulus | | ASTM D638 | 2410 MPa |
tensile strength | Yield | ASTM D638 | 62.1 MPa |
tensile strength | Break | ASTM D638 | 68.3 MPa |
elongation | Yield | ASTM D638 | 6.0 % |
elongation | Break | ASTM D638 | 150 % |
Flexural modulus | | ASTM D790 | 2410 MPa |
bending strength | | ASTM D790 | 96.5 MPa |
Taber abraser | | ASTM D1044 | 45 % |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Impact strength of cantilever beam gap | | ASTM D256 | 850 J/m |
Impact strength of cantilever beam gap | | ASTM D256 | NoBreak |
Dart impact | | ASTM D3763 | 89.3 J |
Impact strength of cantilever beam gap | | ASTM D1822 | 567 kJ/m² |
Electrical performance | Test Condition | Test Method | Test Result |
---|
dielectric constant | | ASTM D150 | 3.00 |
dielectric constant | | ASTM D150 | 3.00 |
Dissipation Factor | | ASTM D150 | 1E-03 |
Dissipation Factor | | ASTM D150 | 2E-03 |
Volume resistivity | | ASTM D257 | 2E+17 ohms·cm |
dielectric strength | | ASTM D149 | 17 kV/mm |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Heat distortion temperature | | ASTM D648 | 145 °C |
Heat distortion temperature | | ASTM D648 | 129 °C |
Heat distortion temperature | | ASTM D648 | 142 °C |
vicat | | ASTM D15255 | 156 °C |
Linear coefficient of thermal expansion | | ASTM D696 | 6.8E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.