Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Specific volume | | ASTMD792 | 0.800 cm³/g |
| melt mass-flow rate | | ASTMD1238 | 7.5 g/10min |
| Shrinkage rate | | 内部方法 | 0.20到0.40 % |
| Water absorption rate | | ASTMD570 | 0.31 % |
| Outdoor applicability | | UL746C | f1 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| UL flame retardant rating | | UL94 | 5VA |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strength 1 | | ASTMD638 | 53.0 Mpa |
| elongation | | ASTMD638 | 15 % |
| Flexural modulus | | ASTMD790 | 3440 Mpa |
| bending strength | | ASTMD790 | 100 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| 23°C | | ASTMD256 | 100 J/m |
| -30°C5 | | ISO180/1A | 9.0 kJ/m² |
| 23°C6 | | ISO180/1A | 10 kJ/m² |
| Suspended wall beam without notch impact strength | | ASTMD4812 | 2100 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| High arc combustion index (HAI) | | UL746 | PLC 1 |
| High Voltage Arc Traceability Rate (HVTR) | | UL746 | PLC 3 |
| Hot wire ignition (HWI) | | UL746 | PLC 1 |
| Volume resistivity | | ASTMD257 | >1.0E+17 ohms·cm |
| dielectric strength | | ASTMD149 | 18 KV/mm |
| Arc resistance 8 | | ASTMD495 | PLC7 |
| Compared to the Leakage Tracking Index (CTI) | | UL746 | PLC 4 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTMD648 | 146 °C |
| Heat distortion temperature | | ASTMD648 | 142 °C |
| vicat | | ASTMD15257 | 154 °C |
| | ASTME831 | 3.2E-05 cm/cm/°C |
| thermal conductivity | | ASTMC177 | 0.20 W/m/K |
| RTI Elec | | UL746 | 120 °C |
| RTI Imp | | UL746 | 110 °C |
| RTI | | UL746 | 125 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.