Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC ML7694-WH8G785 SABIC INNOVATIVE CHONGQING
LEXAN™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/ML7694-WH8G785 |
|---|---|---|---|
| 23°C | ASTMD256 | 100 J/m | |
| 23°C6 | ISO180/1A | 10 kJ/m² | |
| -30°C5 | ISO180/1A | 9.0 kJ/m² | |
| Suspended wall beam without notch impact strength | 23°C | ASTMD4812 | 2100 J/m |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/ML7694-WH8G785 |
|---|---|---|---|
| High arc combustion index (HAI) | HAI | UL746 | PLC 1 |
| Volume resistivity | ASTMD257 | >1.0E+17 ohms·cm | |
| dielectric strength | 3.20mm,inAir | ASTMD149 | 18 KV/mm |
| Hot wire ignition (HWI) | HWI | UL746 | PLC 1 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL746 | PLC 3 |
| Arc resistance 8 | ASTMD495 | PLC7 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL746 | PLC 4 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/ML7694-WH8G785 |
|---|---|---|---|
| elongation | 断裂 | ASTMD638 | 15 % |
| Tensile strength 1 | 断裂 | ASTMD638 | 53.0 Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTMD790 | 100 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTMD790 | 3440 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/ML7694-WH8G785 |
|---|---|---|---|
| UL flame retardant rating | 1.52mm | UL94 | V-0 |
| 2.99mm | UL94 | 5VA |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/ML7694-WH8G785 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.20到0.40 % |
| Water absorption rate | 平衡,23°C | ASTMD570 | 0.31 % |
| melt mass-flow rate | 300°C/1.2kg | ASTMD1238 | 7.5 g/10min |
| Specific volume | ASTMD792 | 0.800 cm³/g | |
| Outdoor applicability | UL746C | f1 |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/ML7694-WH8G785 |
|---|---|---|---|
| MD：-40到95°C | ASTME831 | 3.2E-05 cm/cm/°C | |
| thermal conductivity | ASTMC177 | 0.20 W/m/K | |
| RTI Elec | UL746 | 120 °C | |
| Heat distortion temperature | 1.8MPa,未退火,6.40mm | ASTMD648 | 142 °C |
| vicat | ASTMD15257 | 154 °C | |
| RTI | UL746 | 125 °C | |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm | ASTMD648 | 146 °C |
| RTI Imp | UL746 | 110 °C |