Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.51 g/cm³ |
| Water absorption rate | | | 0.30 % |
| Water absorption rate | | | 0.14 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO2039-2 | 99 |
| | ISO2039-1 | 270 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| UL flame retardant rating | | UL94 | V-0 |
| Limiting Oxygen Index | | ISO4589-2 | 40 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 6300 MPa |
| Tensile stress | | ISO527-2 | 90.0 MPa |
| Tensile strain | | ISO527-2 | 5.0 % |
| compression stress | | ISO604 | 81.0 MPa |
| compression stress | | ISO604 | 41.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 4.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 35 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Dissipation Factor | | IEC60250 | 2E-03 |
| CTI | | IEC60112 | 175 V |
| Surface Resistivity | | IEC60093 | >1.0E+13 ohms |
| Volume resistivity | | IEC60093 | >1.0E+14 ohms·cm |
| dielectric strength | | IEC60243-1 | 24 kV/mm |
| | IEC60250 | 3.20 |
| | IEC60250 | 3.60 |
| Dissipation Factor | | IEC60250 | 1E-03 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 230 °C |
| melting temperature | | | 340 °C |
| | | 3E-05 cm/cm/°C |
| | | 3E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | | 0.30 W/m/K |
| maximum service temperature | | | 250 °C |
| maximum service temperature | | | 310 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.